myTechnical Documents
Details
Product Type
Applications
Industry
Producer
Supplier
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Refractive index | 1.51 | ASTM D542 | |
| Physical Properties | |||
| MFI | 11 | g/10min | ASTM D1238@Load 5.00 kg, Temperature 230 °C |
| Melting range | 218 - 246 | ºC | |
| Specific Gravity | 1.11 | ASTM D792 | |
| Bulk density | 0.650 | g/ml | ASTM D1895 |
| Linear Mold Shrinkage | 0.0040 - 0.0070 | cm/cm | ASTM D951 |
| Thermal Properties | |||
| Heat Deflection temperature | 85.6 | ºC | Annealed; ASTM D648@Thickness 6.35 mm;at 1.8 MPa |
| Thermal Expansion | 86.4 | µm/m-°C | ASTM D696@Temperature 0.000-100.0 °C |
| Vicat softening temperature | 93.9 | ºC | ASTM D1525 |
| Dry Time | 180 - 240 | min | |
| Mechanical Properties | |||
| Tensile modulus-MD | 2960 | MPa | ASTM D638 |
| Flexural strength | 66.9 | MPa | ASTM D790 |
| Flexural modulus-MD | 2210 | MPa | ASTM D790 |
| Elongation at break-MD | 6.0 | % | ASTM D638 |
| Rockwell Hardness | 22 | ASTM D785;Rockwell M | |
| Izod impact strength (notched) | 101 | J/m | bar; ASTM D256@Diameter 6.35 mm |
| Elongation at yield | 4.0 | % | ASTM D638 |
| Tensile Stress at break-MD | 43.4 | MPa | ASTM D638 |
| Izod impact strength (notched) | 64.1 | J/m | bar; ASTM D256@Thickness 6.35 mm, Temperature 0.000 °C |
| Chemical Properties | |||
| Water absorption | <0.30 | % | ASTM D570 |
| Optical Properties | |||
| Haze | 5.0 | % | ASTM D1003 |
| Yellow index | -1.00 | ASTM E313 | |
| Transmittance | 86 | % | ASTM D1003 |
| Process Properties | |||
| Mold Temperature | 48.9 - 76.7 | ºC | |
| Middle Barrel Temperature | 218 - 246 | ºC | Cylinder Temp |
| Drying Temperature | 82.2 | ºC | |