Acrylic-Based Multipolymer Molding Compound.
Details Compound
Product Type
Industry
Producer
Supplier
Advantages
- sterilizable by radiation or ethylene oxide
Other Applications
medical devices
molded applications
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Physical Properties | |||
| Linear Mold Shrinkage | 0.0040 - 0.0070 | cm/cm | ASTM D551 |
| Bulk density | 0.650 | g/ml | ASTM D1895;Apparent Bulk Density |
| MFI | 8.0 | g/10min | ASTM D1238@Load 5.00 kg, Temperature 230 °C |
| Density | 1.11 | g/ml | ASTM D792 |
| Thermal Properties | |||
| Thermal Conductivity | 0.220 | W/mk | |
| Vicat softening temperature | 98.0 | ºC | ASTM D1525 |
| Heat Deflection temperature | 82.0 | ºC | ASTM D648;at 1.8 MPa |
| Specific Heat Capacity | 1.30 | J/gºC | @Temperature 25.0 °C |
| Specific Heat Capacity | 1.90 | J/gºC | @Temperature 100 °C |
| Specific Heat Capacity | 2.30 | J/gºC | @Temperature 175 °C |
| Thermal Expansion | 83.0 | µm/m-°C | ASTM D696@Temperature 20.0 °C |
| Mechanical Properties | |||
| Flexural modulus-MD | 2000 | MPa | ASTM D790 |
| Flexural strength | 62.0 | MPa | ASTM D790; at Yield |
| Tensile modulus-MD | 2100 | MPa | ASTM D638 |
| Elongation at break-MD | 8.3 | % | ASTM D638 |
| Izod impact strength (notched) | 130.0 | J/m | bar; ASTM D256@Diameter 6.35 mm |
| Tensile strength | 38.0 | MPa | ASTM D638;ultimate |
| Elongation at yield | 3.5 | % | ASTM D638 |
| Compressive Strength | 56.0 | MPa | ASTM D695; at Yield |
| Izod impact strength (notched) | 80.0 | J/m | bar; ASTM D256@Diameter 6.35 mm, Temperature 0.000 °C |
| Charpy Impact Strength (notched) | 14.0 | kJ/m² | J/cm; ASTM D256 |
| Optical Properties | |||
| Transmittance | 88 | % | ASTM D1003;visible |
| Haze | 12 | % | ASTM D1003 |