Description: PLEXIGLAS® 7N is a molding compound based on polymethyl methacrylate (PMMA).
Details
Product Type
Producer
Supplier
Advantages
- good flow
- high mechanical strength
- surface hardness
- abrasion resistance
- high light transmission
- excellent weather resistance
- free colorability due to crystal clarity
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Refractive index | 1.49 | ISO 489 | |
Physical Properties | |||
Density | 1.19 | g/ml | ISO 1183 |
MFI | 7.14 | g/10min | ISO 1133@Load 3.80 kg, Temperature 230 °C |
Melting range | 220 - 260 | ºC | |
Thermal Properties | |||
Flameability | IEC 707@Thickness 1.60 mm | ||
Glass transition Temperature | 110 | ºC | IEC 10006 |
Heat Deflection temperature | 95.0 | ºC | ISO 75;at 1.8 MPa |
Heat Deflection temperature | 100 | ºC | ISO 75;at 0.46 MPa |
Dry Time | 120 - 180 | min | Desiccant-type drier |
Vicat softening temperature | 103 | ºC | B50; ISO 306 |
Thermal Expansion | 80.0 | µm/m-°C | ASTM E831@Temperature 0.000 -50.0 °C;Linear |
Mechanical Properties | |||
Tensile modulus-MD | 3200 | MPa | 1mm/min; ISO 527 |
Tensile Stress at break-MD | 73.0 | MPa | 5mm/min; ISO 527 |
Elongation at break-MD | 3.5 | % | 5mm/min; ISO 527 |
(Charpy Impact Strength(unnotched | 20.0 | kJ/m² | ISO 179@Temperature 23.0 °C |
Optical Properties | |||
Transmittance | 92 | % | Transmission Factor; DIN 5036;Visible |
Haze | <0.50 | % | ASTM D1003 |
Process Properties | |||
Mold Temperature | 60.0 - 90.0 | ºC | |
Drying Temperature | <93.0 | ºC | Predrying |