Description: Impact-modified PLEXIGLAS® df22 zk6BR and PLEXIGLAS® df23 zk6BR molding compounds based on PLEXIGLAS® zk6BR are characterized by diffuse scattering of light.
Details
Product Type
Applications
Producer
Supplier
Advantages
- good impact strength
- good weatherability
- high surface hardness
- scratch resistance
- good diffusing power with excellent light transmission
- satin surfaces can be obtained by variation of the extrusion parameters
- high light scattering
- excellent light transmission
Other Applications
lamp covers
projected areas
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Physical Properties | |||
| Density | 1.15 | g/ml | ISO 1183 |
| MFI | 1.495 | g/10min | ISO 1133@Load 3.80 kg, Temperature 230 °C |
| Melting range | 230 - 260 | ºC | |
| Thermal Properties | |||
| Glass transition Temperature | 107 | ºC | IEC 10006 |
| Heat Deflection temperature | 93.0 | ºC | ISO 75; at 1.8 MPa |
| Vicat softening temperature | 91.0 | ºC | B50; ISO 306 |
| Thermal Expansion | 90.0 | µm/m-°C | ASTM E831@Temperature 0.000 -50.0 °C;Linear |
| Heat Deflection temperature | 99.0 | ºC | ISO 75; at 0.46 MPa |
| Dry Time | 120 - 180 | min | Desiccant-type drier |
| Glow WireTest | 700 | ºC | |
| Mechanical Properties | |||
| Tensile modulus-MD | 1900 | MPa | 1mm/min; ISO 527 |
| Elongation at yield | 5.0 | % | 50mm/min; ISO 527 |
| Tensile Stress at yield-MD | 46.0 | MPa | 50mm/min; ISO 527 |
| (Charpy Impact Strength(unnotched | 50.0 | kJ/m² | ISO 179@Temperature 23.0 °C |
| Optical Properties | |||
| Transmittance | 81 | % | Transmission Factor; DIN 5036;Visible |
| Process Properties | |||
| Die Temperature | 260 | ºC | |
| Drying Temperature | <85.0 | ºC | Predrying |