LG Chemical LUPOL HF3308C PP+MF30%, High Impact

کمیت	مقدار	واحد	توضیحات
خواص فیزیکی
Specific Gravity	1.30		ASTM D792
Linear Mold Shrinkage	0.0070 - 0.0090	cm/cm	ASTM D955;Flow@Thickness 3.20 mm
MFI	12	g/10min	ASTM D1238@Load 2.16 kg;Temperature 230 °C
Humidity	<0.010	%	قالب گیری تزریقی
Melting range	200 - 230	ºC	قالب گیری تزریقی
خواص حرارتی
UL RTI	120	ºC	Electrical@Thickness >=1.50 mm
Dry Time	180 - 240	min	قالب گیری تزریقی
Heat Deflection temperature	135	ºC	Unannealed; ASTM D648@Thickness 3.20 mm;at 0.46 MPa
UL RTI	120	ºC	Electrical@Thickness >=3.00 mm
UL RTI	120	ºC	Mechanical with Impact@Thickness >=1.50 mm
UL RTI	120	ºC	Mechanical with Impact@Thickness >=3.00 mm
UL RTI	120	ºC	Mechanical without Impact@Thickness >=1.50 mm
UL RTI	120	ºC	Mechanical without Impact@Thickness >=3.00 mm
Flameability	HB		@Thickness >=1.50 mm
Flameability	HB		@Thickness >=3.00 mm
خواص مکانیکی
Elongation at break-MD	50	%	50mm/min; ASTM D638@Thickness 3.20 mm
Flexural strength	40.7	MPa	Yield;30mm/min; ASTM D790@Thickness 6.40 mm
Tensile Stress at yield-MD	24.5	MPa	50mm/min; ASTM D638@Thickness 3.20 mm
Izod impact strength (notched)	>52	J/m	ASTM D256@Thickness 6.4 mm, Temperature 23.0 °C
Flexural modulus-MD	2840	MPa	30mm/min; ASTM D790@Thickness 6.40 mm
خواص فرایندی
Drying Temperature	70.0 - 80.0	ºC	قالب گیری تزریقی
Middle Barrel Temperature	200 - 230	ºC	قالب گیری تزریقی
Mold Temperature	40.0 - 60.0	ºC	قالب گیری تزریقی