این پلیمر، تاخیر دهنده ی شعله است و گرید قالب گیری تزریقی می باشد.
جزئیات
CAS
9003-56-9
حوزه کاربردی
تولید کننده
داده های فنی
کمیت | مقدار | واحد | توضیحات |
---|---|---|---|
خواص فیزیکی | |||
Humidity | <2 | % | |
Specific Gravity | 1.18 | ||
Linear Mold Shrinkage | 0.004 - 0.006 | cm/cm | Thickness 3.2 mm |
MFI | 20 | g/10min | 250°C/2.16Kg |
خواص حرارتی | |||
Flameability | V-0 | Thickness 3- mm | |
Flameability | V-0 | Thickness 2.5- mm | |
Flameability | V-0 | Thickness 2- mm | |
Flameability | V-0 | Thickness 1.5- mm | |
Flameability | V-0 | Thickness 1.2- mm | |
UL RTI | 85 | ºC | Mechanical without Impact-Thickness 3- mm |
UL RTI | 85 | ºC | Mechanical without Impact-Thickness 2.5- mm |
UL RTI | 85 | ºC | Mechanical without Impact-Thickness 2- mm |
UL RTI | 85 | ºC | Mechanical without Impact-Thickness 1.5- mm |
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 1.2- mm |
UL RTI | 80 | ºC | Mechanical with Impact-Thickness 3- mm |
UL RTI | 80 | ºC | Mechanical with Impact-Thickness 2.5- mm |
UL RTI | 80 | ºC | Mechanical with Impact-Thickness 2- mm |
UL RTI | 80 | ºC | Mechanical with Impact-Thickness 1.5- mm |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 1.2- mm |
UL RTI | 80 | ºC | Electrical-Thickness 3- mm |
UL RTI | 80 | ºC | Electrical-Thickness 2.5- mm |
UL RTI | 80 | ºC | Electrical-Thickness 2- mm |
UL RTI | 80 | ºC | Electrical-Thickness 1.5- mm |
UL RTI | 60 | ºC | Electrical-Thickness 1.2- mm |
Dry Time | 180 - 300 | min | |
Flameability | 5VA | Thickness 1.5- mm | |
Flameability | 5VA | Thickness 2- mm | |
Flameability | 5VA | Thickness 2.5- mm | |
Flameability | 5VA | Thickness 3- mm | |
خواص مکانیکی | |||
Izod impact strength (notched) | 343 | J/m | Thickness 3.2 mm |
Flexural modulus-MD | 2647.79 | MPa | Thickness 6.4 mm |
Flexural strength | 93.16 | MPa | Thickness 6.4 mm |
Tensile strength | 58.84 | MPa | Thickness 3.2 mm |
Elongation at break-MD | >80 | % | Thickness 3.2 mm |
Rockwell Hardness | 113 | ||
خواص الکتریکی | |||
Hot Wire Ignition | 30 - 60 | s | Thickness 1.2- mm |
Hot Wire Ignition | 30 - 60 | s | Thickness 1.5- mm |
Hot Wire Ignition | 30 - 60 | s | Thickness 2- mm |
Arc Resistance | 60 - 120 | s | |
HAI)High Amp Arc Ignition) | >120 | arcs | Thickness 1.5 mm |
HAI)High Amp Arc Ignition) | >120 | arcs | Thickness 2 mm |
Comparative Tracking Index | 250 - 400 | V | |
خواص فرایندی | |||
Middle Barrel Temperature | 235 - 255 | ºC | |
Mold Temperature | 50 - 80 | ºC | |
Drying Temperature | 75 - 85 | ºC |