CYREX 100 alloy has the lowest impact strength of the CYREX alloy grades with 8.0 fppi for notched Izod impact at room temperature.
Детали
зая́вки
Режиссер
поставщиком
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Физические свойства | |||
| Linear Mold Shrinkage | 0.0040 - 0.0080 | cm/cm | ASTM D551 |
| MFI | 4.0 | g/10min | ASTM D1238@Load 3.80 kg, Temperature 230 °C |
| Specific Gravity | 1.12 | ASTM D792 | |
| Тепловые свойства | |||
| Thermal Expansion | 93.6 | µm/m-°C | ASTM D696@Temperature 0.000 -100 °C;linear |
| Vicat softening temperature | 119 | ºC | ASTM D1525 |
| Heat Deflection temperature | 95.0 | ºC | ASTM D648; at 1.8 MPa |
| Flameability | |||
| Механические свойства | |||
| Flexural strength | 79.3 | MPa | ASTM D790 |
| Elongation at yield | 3.7 | % | ASTM D638 |
| Rockwell Hardness | 45 | Rockwell M; ASTM D785 | |
| Tensile modulus-MD | 2100 | MPa | ASTM D638 |
| Tensile Stress at yield-MD | 48.3 | MPa | ASTM D638 |
| Elongation at break-MD | 31 | % | ASTM D638 |
| Izod impact strength (notched) | 427 | J/m | @Thickness 3.17 mm, Temperature 22.8 °C |
| Химические свойства | |||
| Water absorption | <0.26 | % | ASTM D570 |