Farapol O 117 is an Unsaturated Polyester Resin based on Orthophthalic Anhydride and standard Glycols, dissolved in and cross linked with Styrene having capability to be used as casting and laminating resin for General Purpose items.
Детали
Orthophthalic Anhydride
- Medium Reactivity
- Good Laminating & wetting properties
- Good Mechanical performance combining a good elongation at break in tension and a suitable HDT
Manufacturing of Decorative items, sheets & architectural panels. Special for Colorless Items
Filled Resin objects
FARAPOL O 117 is a product sensitive to temperature, Light & Oxidation. Hence should be stored indoors in dry place at a temperature between 5 and 25°C. Keep always in the original,unopened and undamaged containers. Avoid keeping material exposed to sunlight.
Avoid storing the resin along with Metallic Driers and Peroxides in the same area.
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Свойства внешнего вида | |||
| Color | <1 | Gardner | |
| Физические свойства | |||
| Shrinkage | Almost 2 | % | |
| Solid Content | 61 ± 1 | % | |
| Specific Gravity | 1.110 - 1.113 | ||
| Viscosity | 350 ± 30 | cP | 25 °C |
| Тепловые свойства | |||
| Heat Deflection temperature | >80 | ºC | ISO527-2 |
| Механические свойства | |||
| Elongation at break-MD | >3 | % | ISO527-2 |
| Tensile strength | >70 | MPa | ISO527-2 |
| barcol hardness | >40 | ASTM D2583 | |
| Flexural strength | >110 | MPa | ISO178 |
| Химические свойства | |||
| Water absorption | Approximately 0.25 | % | ISO62- Test Method 3 |
| Gel time | 1020 ± 60 | sec. | 25 °C |
| Acidity number | 20 - 30 | mg KOH/g | |