INFINO® NH-1015V is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy.Can be processed using injection molding.
Детали
Тип продукта
Промышленность
Режиссер
Дреимущества
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
Другие приложения
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Свойства внешнего вида | |||
| Appearance | Natural colors | ||
| Physical state | Pill | ||
| Физические свойства | |||
| Shrinkage | 0.5 - 0.7 | % | (ASTM D955;Flow, 3.2 mm (MD |
| Humidity | <0.05 | % | |
| MFI | 30 | g/10min | ISO 1133;220℃/10kg |
| Density | 1.17 | g/ml | ISO 1183 |
| Тепловые свойства | |||
| Glow WireTest | 800 | ºC | Glow Wire Ignition Temperature;IEC 60695-2-13;1.3 mm, 2.1 mm, 2.5 mm, 3.0 mm |
| Glow WireTest | 775 | ºC | Glow Wire Ignition Temperature;IEC 60695-2-13;1.0 mm, 1.5 mm |
| Glow WireTest | 960 | ºC | Glow Wire Flammability Index;IEC 60695-2-12;1.0 mm, 1.3 mm, 1.5 mm, 2.1 mm, 2.5 mm, 3.0 mm |
| UL RTI | 90 | ºC | Mechanical without Impact, 1.5 mm, 2.0 mm, 2.1 mm, 2.5 mm, 3.0 mm |
| UL RTI | 85 | ºC | Mechanical with Impact, 1.5 mm, 2.0 mm, 2.1 mm, 2.5 mm, 3.0 mm |
| UL RTI | 90 | ºC | Electric, 1.5 mm, 2.0 mm, 2.1 mm, 2.5 mm, 3.0 mm |
| Heat Deflection temperature | 102 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 97 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 94 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Dry Time | 240 - 360 | min | |
| Dry Time | 120 - 240 | min | |
| UL RTI | 60 | ºC | Mechanical without Impact, 1.0 mm, 1.2 mm, 1.3 mm |
| UL RTI | 60 | ºC | Mechanical with Impact, 1.0 mm, 1.2 mm, 1.3 mm |
| Vicat softening temperature | 103 | ºC | ISO R 306;B/120 |
| UL RTI | 60 | ºC | Electric, 1.0 mm, 1.2 mm, 1.3 mm |
| Vicat softening temperature | 100 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 82 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Механические свойства | |||
| Rockwell Hardness | 118 | ISO 2039-2;R Scale | |
| Charpy Impact Strength (notched) | 17 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| (Izod impact strength(notched | 14 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Flexural strength | 89 | MPa | ISO 178;2mm/min |
| Flexural modulus-MD | 2550 | MPa | ISO 178;2mm/min |
| Tensile Stress at break-MD | 48 | MPa | ISO 527;50mm/min |
| Strain at break-MD | 45 | % | ISO 527;50mm/min |
| Tensile modulus-MD | 2500 | MPa | ISO 527;50mm/min |
| Tensile Stress at yield-MD | 61 | MPa | ISO 527;50mm/min |
| Химические свойства | |||
| Decomposition temperature | >400 | ºC | |
| Электрические свойства | |||
| HAI)High Amp Arc Ignition) | 3 | arcs | 1.5mm |
| Comparative Tracking Index | V | ||
| Hot Wire Ignition | 2 | s | 1.5mm |