myТехнические документы
PS, Impact Modified.
Детали
CAS
9003-55-8
Тип продукта
Режиссер
Дреимущества
- High Gloss
Другие приложения
Electric/Electronic Components
Stationary Articles
Food Containers
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Физические свойства | |||
| Melting range | 190 - 220 | ºC | injection molding |
| Humidity | <0.01 | % | injection molding |
| MFI | 8 | g/10min | Temperature 200 °C, ASTM D1238(G) |
| Specific Gravity | 1.05 | ASTM D792 | |
| Linear Mold Shrinkage | 0.004 - 0.008 | cm/cm | ASTM D955 |
| MFI | 99 | g/10min | Temperature 220 °C, Load 10 kg, ASTM D1238(G) |
| MFI | 23 | g/10min | Temperature 230 °C, Load 3.8 kg, ASTM D1238 (I) |
| Тепловые свойства | |||
| Dry Time | 120 - 240 | min | injection molding |
| Heat Deflection temperature | 83 | ºC | Unannealed; ASTM D648, 1.8 MPa (264 psi) |
| Vicat softening temperature | 95 | ºC | Load 5 kg, 50°C/h; ASTM D 1525 |
| UL RTI | 50 | ºC | Thickness 1.5,3 mm, Electrical |
| UL RTI | 50 | ºC | Thickness 1.5,3 mm, Mechanical with Impact |
| UL RTI | 50 | ºC | Thickness 1.5,3 mm, Mechanical without Impact |
| Flameability | Thickness 1.5,3 mm | ||
| Механические свойства | |||
| Tensile strength | 41.1 | MPa | Yield, hickness 3.2 mm, 50 mm/min ; ASTM D638 |
| Elongation at break-MD | 34 | % | hickness 3.2 mm, 50 mm/min ; ASTM D638 |
| Elongation at yield | 6 | % | hickness 3.2 mm, 50 mm/min ; ASTM D638 |
| Tensile modulus-MD | 2471.2 | MPa | Thickness 3.2 mm, 1 mm/min; ASTM D638 |
| Flexural strength | 73.5 | MPa | Yield, Thickness 3.2 mm, 15 mm/min; ASTM D 790 |
| Flexural modulus-MD | 2863.5 | MPa | Thickness 3.2 mm, 15 mm/min; ASTM D 790 |
| Rockwell Hardness | 117 | ASTM D 785 | |
| Электрические свойства | |||
| Hot Wire Ignition | 15 - 30 | s | Thickness 3- mm |
| HAI)High Amp Arc Ignition) | >120 | arcs | Thickness 3 mm |
| Arc Resistance | 120 - 180 | s | ASTM D 495 |
| Dielectric Strength | 40 | Kv/mm | |
| Volume resistance | 1e+014 | ohm-cm | |
| Hot Wire Ignition | 7 - 15 | s | Thickness 1.5- mm |
| HAI)High Amp Arc Ignition) | 60 - 120 | arcs | Thickness 1.5 mm |
| Свойства процесса | |||
| Mold Temperature | 40 - 70 | ºC | injection molding |
| Drying Temperature | 80 | ºC | injection molding |
| Middle Barrel Temperature | 180 - 200 | ºC | injection molding |