Injection Molding, PC/ABS, Halogen Free Flame Retardant, High strength
Детали
CAS
9003-56-9
Режиссер
Технические данные
Количество | Стоимость | Е диница измерения | 3амечание |
---|---|---|---|
Физические свойства | |||
Humidity | <2 | % | |
Specific Gravity | 1.27 | ||
MFI | 12 | g/10min | 260°C/2.16Kg |
Linear Mold Shrinkage | 0.002 - 0.004 | cm/cm | Thickness 3.2 mm |
Тепловые свойства | |||
Flameability | Thickness 3- mm | ||
UL RTI | 60 | ºC | Mechanical without Impact |
Flameability | Thickness 1- mm | ||
UL RTI | 60 | ºC | Mechanical with Impact |
UL RTI | 60 | ºC | Electrical |
Dry Time | 180 - 240 | min | |
Механические свойства | |||
Izod impact strength (notched) | >58.8 | J/m | Thickness 3.2 mm |
Flexural modulus-MD | 4216.85 | MPa | Thickness 6.4 mm |
Flexural strength | 107.87 | MPa | Thickness 6.4 mm |
Tensile strength | 62.76 | MPa | Thickness 3.2 mm |
Elongation at break-MD | 30 | % | Thickness 3.2 mm |
Свойства процесса | |||
Middle Barrel Temperature | 245 - 265 | ºC | |
Mold Temperature | 60 - 80 | ºC | |
Drying Temperature | 75 - 85 | ºC |