myAmong the characteristics of LUPOY polycarbonate resins are excellent mechanical properties, high heat resistance, high impact strength, and dimensional stability.
Детали
Режиссер
Дреимущества
- excellent mechanical properties
- high heat resistance
- high impact strength
- dimensional stability
Другие приложения
Automotive: Automotive front ends, cluster pad main panel (instrument panel), lower cluster pad main, console box, glove box cover, door, wheel cover and cap, defroster grill, back mirror housing
Electrical and Electronic: Monitor housing, fax housing, notebook PC housing, cellular phone case, fax and copy machine frame, CD ROM drive tray and main frame, relay case, connector
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Физические свойства | |||
| Specific Gravity | 1.18 | ||
| MFI | 22 | g/10min | 250°C/2.16Kg |
| Linear Mold Shrinkage | 0.006 | cm/cm | ASTM D955 , Transverse |
| Linear Mold Shrinkage | 0.004 | cm/cm | ASTM D955 |
| Melting range | 230 - 260 | ºC | |
| Тепловые свойства | |||
| Dry Time | 240 - 360 | min | |
| Heat Deflection temperature | 88 | ºC | ASTM D648 |
| Flameability | Thickness 1.5 mm | ||
| Механические свойства | |||
| Izod impact strength (notched) | 390 | J/m | ASTM D256 |
| Flexural modulus-MD | 2350 | MPa | ASTM D 790 |
| Flexural strength | 79 | MPa | ASTM D 790 |
| Tensile strength | 55 | MPa | ASTM D638 |
| Elongation at break-MD | 50 | % | ASTM D638 , Thickness 3.2 mm |
| Rockwell Hardness | 113 | ASTM D 785 | |
| Свойства процесса | |||
| Middle Barrel Temperature | 210 - 240 | ºC | |
| Mold Temperature | 50 - 80 | ºC | |
| Drying Temperature | 60 - 80 | ºC | |