Injection Molding, PC/ABS, Halogen Free Flame Retardant
Детали
CAS
9003-56-9
Режиссер
Технические данные
Количество | Стоимость | Е диница измерения | 3амечание |
---|---|---|---|
Физические свойства | |||
Humidity | <2 | % | |
Specific Gravity | 1.19 | ||
MFI | 8 | g/10min | 250°C/2.16Kg |
Linear Mold Shrinkage | 0.005 - 0.008 | cm/cm | Thickness 3.2 mm |
Тепловые свойства | |||
Flameability | Thickness 1.5- mm | ||
Flameability | Thickness 3- mm | ||
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 1.5- mm |
UL RTI | 60 | ºC | Mechanical without Impact-Thickness 3- mm |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 3- mm |
UL RTI | 60 | ºC | Mechanical with Impact-Thickness 1.5- mm |
UL RTI | 60 | ºC | Electrical-Thickness 3- mm |
UL RTI | 60 | ºC | Electrical-Thickness 1.5- mm |
Dry Time | 180 - 240 | min | |
Механические свойства | |||
Izod impact strength (notched) | 686 | J/m | Thickness 3.2 mm |
Flexural modulus-MD | 2353.59 | MPa | Thickness 6.4 mm |
Flexural strength | 99.04 | MPa | Thickness 6.4 mm |
Tensile strength | 61.78 | MPa | Thickness 3.2 mm |
Elongation at break-MD | 50 | % | Thickness 3.2 mm |
Свойства процесса | |||
Middle Barrel Temperature | 240 - 255 | ºC | |
Mold Temperature | 50 - 80 | ºC | |
Drying Temperature | 75 - 85 | ºC |