Injection Molding, PC/ABS, Halogen Free Flame Retardant, General Purpose Application
Детали
CAS
9003-56-9
Режиссер
Технические данные
Количество | Стоимость | Е диница измерения | 3амечание |
---|---|---|---|
Физические свойства | |||
Humidity | <2 | % | |
Specific Gravity | 1.18 | ||
Linear Mold Shrinkage | 0.005 - 0.008 | cm/cm | Thickness 3.2 mm |
MFI | 20 | g/10min | 250°C/2.16Kg |
Тепловые свойства | |||
UL RTI | 80 | ºC | Mechanical with Impact |
UL RTI | 80 | ºC | Electrical |
Dry Time | 180 - 240 | min | |
UL RTI | 85 | ºC | Mechanical without Impact |
Flameability | Thickness 1.2- mm | ||
Flameability | Thickness 2.5- mm | ||
Flameability | Thickness 3- mm | ||
Механические свойства | |||
Izod impact strength (notched) | 118 | J/m | Thickness 3.2 mm |
Flexural modulus-MD | 2745.86 | MPa | Thickness 6.4 mm |
Flexural strength | 98.06 | MPa | Thickness 6.4 mm |
Tensile strength | 65.70 | MPa | Thickness 3.2 mm |
Elongation at break-MD | 80 | % | Thickness 3.2 mm |
Свойства процесса | |||
Middle Barrel Temperature | 250 - 270 | ºC | |
Mold Temperature | 70 - 90 | ºC | |
Drying Temperature | 85 - 95 | ºC |