myInjection Molding, PC/ABS, Flame Retardance, Heat Resistance
Детали
CAS
9003-56-9
Режиссер
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Физические свойства | |||
| Humidity | <2 | % | |
| Specific Gravity | 1.18 | ||
| Linear Mold Shrinkage | 0.004 - 0.006 | cm/cm | |
| MFI | 5 | g/10min | 250°C/2.16Kg |
| Тепловые свойства | |||
| Flameability | Thickness 3- mm | ||
| Flameability | Thickness 3- mm | ||
| Flameability | Thickness 1.5- mm | ||
| UL RTI | 70 | ºC | Mechanical without Impact-Thickness 3- mm |
| UL RTI | 70 | ºC | Mechanical without Impact-Thickness 1.5- mm |
| UL RTI | 70 | ºC | Mechanical without Impact-Thickness 0.82- mm |
| UL RTI | 65 | ºC | Mechanical with Impact-Thickness 3- mm |
| UL RTI | 65 | ºC | Mechanical with Impact-Thickness 1.5- mm |
| UL RTI | 65 | ºC | Mechanical with Impact-Thickness 0.82- mm |
| UL RTI | 85 | ºC | Electrical-Thickness 1.5- mm |
| UL RTI | 85 | ºC | Electrical-Thickness 3- mm |
| UL RTI | 85 | ºC | Electrical-Thickness 0.82- mm |
| Dry Time | 180 - 300 | min | |
| Механические свойства | |||
| Rockwell Hardness | 113 | ||
| Izod impact strength (notched) | 588 | J/m | Temperature 23 °C |
| Flexural strength | 82.37 | MPa | Thickness 3.2 mm |
| Flexural modulus-MD | 2353.59 | MPa | Thickness 3.2 mm |
| Tensile strength | 53.93 | MPa | Thickness 3.2 mm |
| Elongation at break-MD | 50 | % | Thickness 3.2 mm |
| Электрические свойства | |||
| Volume resistance | 1e+011 | ohm-cm | |
| Dielectric Strength | 38 | Kv/mm | |
| Arc Resistance | 60 - 120 | s | |
| HAI)High Amp Arc Ignition) | >120 | arcs | Thickness 1.5 mm |
| HAI)High Amp Arc Ignition) | >120 | arcs | Thickness 3 mm |
| Hot Wire Ignition | 30 - 60 | s | Thickness 3- mm |
| Hot Wire Ignition | 7 - 15 | s | Thickness 1.5- mm |
| Hot Wire Ignition | 7 - 15 | s | Thickness 0.82- mm |
| Свойства процесса | |||
| Middle Barrel Temperature | 235 - 255 | ºC | |
| Mold Temperature | 50 - 80 | ºC | |
| Drying Temperature | 75 - 85 | ºC | |