Injection Molding, PC/ABS, General Purpose, High Impact at Low Temperature, High Flow, Heat Resistance.
Детали
CAS
103598-77-2 , 9003-56-9
Промышленность
Режиссер
Дреимущества
- High Flow
- High Impact
- Heat Resistance
Другие приложения
Mobile Phone Housing
Технические данные
Количество | Стоимость | Е диница измерения | 3амечание |
---|---|---|---|
Физические свойства | |||
Humidity | <0.02 | % | |
Specific Gravity | 1.14 | ASTM D792 | |
Linear Mold Shrinkage | 0.004 - 0.006 | cm/cm | ASTM D955 |
MFI | 5 | g/10min | ASTM D 1238 , Temperature 250 °C -Load 2.16 kg |
Melting range | 255 - 285 | ºC | Injection Molding |
Тепловые свойства | |||
Flameability | Thickness 0.75- mm | ||
Dry Time | 180 - 300 | min | Injection Molding |
UL RTI | 60 | ºC | Electrical |
UL RTI | 60 | ºC | Mechanical with Impact |
UL RTI | 60 | ºC | Mechanical without Impact |
Механические свойства | |||
Izod impact strength (notched) | 588 | J/m | ASTM D256-Temperature 23 °C |
Izod impact strength (notched) | J/m | ASTM D256-Temperature -30 °C | |
Flexural modulus-MD | 2255.52 | MPa | ASTM D 790 |
Flexural strength | 88.25 | MPa | ASTM D 790 |
Tensile strength | 54.91 | MPa | ASTM D638 |
Elongation at break-MD | 100 | % | ASTM D638 |
Rockwell Hardness | 111 | ASTM D 785 | |
Свойства процесса | |||
Drying Temperature | 80 - 100 | ºC | Injection Molding |
Mold Temperature | 80 - 100 | ºC | Injection Molding |
Middle Barrel Temperature | 250 - 280 | ºC | Injection Molding |