Acrylonitrile butadiene styrene (ABS) /Polybutylene Terephthalate (PBT) alloy with 10% Glass Fiber. It is suitable for processing through injection molding.
Детали Соединение
CAS
9003-56-9, 68928-70-1, 65997-17-3, 24968-12-5, 9003-54-7 ;1309-64-4
Тип продукта
Усиленный с
Промышленность
Режиссер
Дреимущества
- Flame Retardant
- Impact Modified
- Dimensional Stability
Другие приложения
Electric & Electronic Products (Switch)
Технические данные
Количество | Стоимость | Е диница измерения | 3амечание |
---|---|---|---|
dry Time | 4 - 5 | hr | |
Физические свойства | |||
Melting range | 240 - 250 | ºC | |
Humidity | <0.02 | % | |
Linear Mold Shrinkage | 0.0040 - 0.0090 | cm/cm | ASTM D955;(Flow), 3.2mm |
Specific Gravity | 1.40 | ASTM D792 | |
Тепловые свойства | |||
Flameability | UL94;Thickness >=3.00 mm | ||
Flameability | UL94;Thickness >=1.50 mm | ||
UL RTI | 60 | ºC | Thickness >=3.00 mm;Mechanical without Impact |
UL RTI | 60 | ºC | Thickness >=1.50 mm;Mechanical without Impact |
UL RTI | 60 | ºC | Thickness >=1.50 mm;Mechanical with Impact |
UL RTI | 60 | ºC | Thickness >=3.00 mm;Mechanical with Impact |
UL RTI | 60 | ºC | Thickness >=3.00 mm;Electrical |
UL RTI | 60 | ºC | Thickness >=1.50 mm;Electrical |
Heat Deflection temperature | 110 | ºC | ASTM D648;6.4mm;(Unannealed);at 1.8 MPa |
Melting point | 225 | ºC | Peak at Break |
Механические свойства | |||
Elongation at break-MD | 3 | % | ASTM D638;5mm/min;3.2mm |
Flexural strength | 83.4 | MPa | ASTM D790;1.3mm/min;3.2mm;Yield |
Flexural modulus-MD | 2940 | MPa | ASTM D790;1.3mm/min;3.2mm |
Izod impact strength (notched) | 58.8 | J/m | ASTM D256;23℃;3.2mm |
Tensile Stress at yield-MD | 55.9 | MPa | ASTM D638;5mm/min;3.2mm |
Электрические свойства | |||
HAI)High Amp Arc Ignition) | 30 - 60 | arcs | Thickness 3.00 mm |
Hot Wire Ignition | 15 - 30 | s | Thickness >=1.50 mm |
Hot Wire Ignition | 30 - 60 | s | Thickness >=3.00 mm |
HAI)High Amp Arc Ignition) | 60 - 120 | arcs | Thickness 1.50 mm |
Arc Resistance | 60 - 120 | s | ASTM D495 |
Volume resistance | 1.00e+15 | ohm-cm | ASTM D257 |
Dielectric Strength | 26 | Kv/mm | ASTM D149;Thickness 1.00 mm |
Comparative Tracking Index | 175 | V | Solution A; IEC 60112 |
Свойства процесса | |||
Middle Barrel Temperature | 230 - 245 | ºC | |
Mold Temperature | 60 - 90 | ºC | |
Drying Temperature | 100 | ºC |