Технические документы
Description: ROHACELL® is produced by thermal expansion of a co-polymer sheet of methacrylic acid and methacrylonitrile. During the foaming process the copolymer sheet is converted to PMI- PolyMethacrylImide. Alcohol is used as a blowing agent,thus ROHACELL® contains no fluorinated carbon hydrates and is halogen free. Information provided by degussa.
Детали
Тип продукта
Режиссер
поставщиком
Дреимущества
- very homogeneous cell structure
- isotropic properties
- Extended Temperature
- closed-cell rigid foam plastic based on PMI (polymethacrylimide)
- does not contain any CFCs
- serves as a core material in advanced BMI-sandwich parts
- easy to shape
- Thermoformability
- Curing temperature up to 190C (374F)
- Curing pressure up to 0.7 Mpa (100 psi)
- post-curing temperature (free-standing) up to 230C (446 F)
- Sandwich components using ROHACELL® XT as a core material can be realized in a single work step (=cocuring). The structural components can be manufactured in an autoclave and by means of RTM.
Другие приложения
used in aircraft and space construction
Технические данные
Количество | Стоимость | Е диница измерения | 3амечание |
---|---|---|---|
Физические свойства | |||
Density | 0.110 | g/ml | DIN 53420, ISO 845, ASTM D 1622 |
Тепловые свойства | |||
Maximum Service Temperature | 240 | ºC | Heat Distortion Resistance; DIN 53424; Air |
Механические свойства | |||
shear modulus | 63 | MPa | DIN 53294, ASTM C 273 |
Tensile Stress at break-MD | 3.70 | MPa | DIN 53455, ISO 527-2, ASTM D 638 |
Elongation at break-MD | 4.0 | % | DIN 53455, ISO 527-2, ASTM D 638 |
Tensile modulus-MD | 180 | MPa | ISO 527-2, ASTM D 638 |
Compressive Strength | 3.60 | MPa | DIN 53421, ISO 844, ASTM D 1621 |
shear strength | 2.10 | MPa | DIN 53294, ASTM C 273 |