Medium viscosity, easily demoldable, 30% glass fiber–reinforced, heat-stabilized polyamide 1010 compound. Due to its mold release properties, VESTAMID Terra DS18-GF30 is suitable for the efficient production of injection molded parts with short cycle times.
Детали Соединение
Тип продукта
Усиленный с
Режиссер
поставщиком
Химический состав
the polycondensation product of 1,10-decamethylene diamine (D) and 1,10-decanedioic acid (sebacic acid—S)
Дреимущества
- Durable
- Heat stabilized
- Renewable Resource Content
- Good Dimensional stability
- High Dimensional Stability
Технические данные
Количество | Стоимость | Е диница измерения | 3амечание |
---|---|---|---|
Свойства внешнего вида | |||
Appearance | Granvl- cylindrical | ||
Физические свойства | |||
Density | 1.29 | g/ml | ISO 1183, 23°C |
Melting range | 210 - 240 | ºC | |
Тепловые свойства | |||
Vicat softening temperature | 196 | ºC | ISO 306, 50 N |
Vicat softening temperature | 201 | ºC | ISO 306, 10 N |
Melting point | 206 | ºC | ISO 11357, 2nd heating, DSC |
Dry Time | 120 - 240 | min | |
Механические свойства | |||
Strain at break-MD | 5 | % | ISO 527-1 |
Tensile Stress at yield-TD | 136 | Mpa | ISO 527-2 |
Strain at break-MD | 5 | % | ISO 527-2 |
Tensile modulus-MD | 7400 | MPa | ISO 527-1 |
(Charpy Impact Strength(unnotched | 95 | kJ/m² | ISO 179/1eU, 23°C, Complete break, incl. hinge break H |
Charpy Impact Strength (notched) | 19 | kJ/m² | ISO 179/1eA, 23°C, Complete break, incl. hinge break H |
(Charpy Impact Strength(unnotched | 96 | kJ/m² | ISO 179/1eU, -30°C, Complete break, incl. hinge break H |
viscosity number | 180 | ml/g | ISO 307 |
Tensile Stress at yield-TD | 136 | Mpa | ISO 527-1 |
Charpy Impact Strength (notched) | 11 | kJ/m² | ISO 179/1eA, -30°C, Complete break, incl. hinge break H |
Tensile modulus-MD | 7400 | MPa | ISO 527-2 |
Химические свойства | |||
Water absorption | 1.4 | % | ISO 62, at Saturation |
Свойства процесса | |||
Mold Temperature | 60 - 100 | ºC | |
Drying Temperature | 80 - 100 | ºC |