| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Свойства внешнего вида | |||
| Appearance | White | ||
| Физические свойства | |||
| Melting range | 221 - 226 | ºC | DSC |
| Linear Mold Shrinkage | 0.019 | cm/cm | Transverse-Pigmentation can change mold shrinkage. |
| MFI | 52.5 | g/10min | ISO 1133@Load 2.16 kg,Temperature 250 °C |
| Density | 1.50 | g/ml | ISO 1183 |
| Linear Mold Shrinkage | 0.019 | cm/cm | Pigmentation can change mold shrinkage. |
| Тепловые свойства | |||
| Flameability | @Thickness 0.800 mm | ||
| Flameability | @Thickness 1.60 mm | ||
| Heat Deflection temperature | 185 | ºC | ISO 75-1/2-at 0.46 MPa |
| Thermal Expansion | 110 | µm/m-°C | Longitudinal; ISO 11359@Temperature 23.0-55.0 °C |
| Heat Deflection temperature | 80.0 | ºC | ISO 75-1/2-at 1.8 MPa |
| Vicat softening temperature | 192 | ºC | 50N; ISO 306 |
| Vicat softening temperature | 216 | ºC | 10N; ISO 306 |
| Thermal Expansion | 110 | µm/m-°C | Transverse to Flow; ISO 11359@Temperature 23.0-55.0 °C |
| Flameability | @Thickness 0.400 mm | ||
| Механические свойства | |||
| Hardness Shore D | 81 | ISO 868 | |
| Ball indentation Hardness | 160 | MPa | H30; ISO 2039-1 |
| Tensile Stress at break-MD | 55.0 | MPa | 5 mm/min; ISO 527-1/2 |
| Elongation at break-MD | 3.0 | % | 5 mm/min; ISO 527-1/2 |
| (Charpy Impact Strength(unnotched | 25 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
| Tensile modulus-MD | 3100 | MPa | ISO 527-1/2 |
| (Charpy Impact Strength(unnotched | 25 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
| Charpy Impact Strength (notched) | 3 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
| Charpy Impact Strength (notched) | 3 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
| Химические свойства | |||
| Oxirane Oxygen Content | 32 | % | ISO 4589 |
| Water absorption | 0.40 | % | ISO 62 -at Saturation |
| Electrolytic Corrosion | IEC 60426 | ||
| Электрические свойства | |||
| Comparative Tracking Index | 225 | V | Test Solution A, 100 drops; IEC 60112 |
| Dissipation Factor | 0.020 | IEC 60250@Frequency 1e+6 Hz | |
| Volume resistance | 1.00e+15 | ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 | ohm | IEC 60093 |
| Dielectric Constant | 3.4 | IEC 60250@Frequency 1e+6 Hz | |
| Dielectric Constant | 3.4 | IEC 60250@Frequency 100 Hz | |
| Dielectric Strength | 27.0 | Kv/mm | K20/P50; IEC 60243-1 |
| Dissipation Factor | 0.0020 | IEC 60250@Frequency 100 Hz | |
| Comparative Tracking Index | 250 | V | Test Solution A, CTI; IEC 60112 |