myТехнические документы
Детали
Тип продукта
Режиссер
поставщиком
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Физические свойства | |||
| MFI | 62.88 | g/10min | ISO 1133@Load 2.16 kg,Temperature 250 °C |
| Density | 1.31 | g/ml | ISO 1183 |
| Linear Mold Shrinkage | 0.015 | cm/cm | sheet with film gate at rim, mold temperature 80°C@Thickness 2.00 mm |
| Linear Mold Shrinkage | 0.015 | cm/cm | Transverse |
| Тепловые свойства | |||
| Flameability | @Thickness 0.800 mm | ||
| Flameability | @Thickness 1.60 mm | ||
| Thermal Expansion | 100 | µm/m-°C | Longitudinal; ISO 11359,DIN 53752@Temperature 23.0-55.0 °C |
| Heat Deflection temperature | 170 | ºC | ISO 75-1/-2-at 0.46 MPa |
| Heat Deflection temperature | 60.0 | ºC | ISO 75-1/-2-at 1.8 MPa |
| Vicat softening temperature | 190 | ºC | Method B, 50 N; ISO 306 |
| Thermal Expansion | 100 | µm/m-°C | Transverse to Flow; ISO 11359,DIN 53752@Temperature 23.0-55.0 °C |
| Vicat softening temperature | 220 | ºC | Method A, 10 N; ISO 306 |
| Механические свойства | |||
| Elongation at yield | 8.0 | % | ISO 527-1/2 |
| Tensile Stress at yield-MD | 60.0 | MPa | ISO 527-1/2 |
| Elongation at break-MD | 15 | % | ISO 527-1/2 |
| Tensile modulus-MD | 2700 | MPa | ISO 527-1/-2 |
| (Charpy Impact Strength(unnotched | 140 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
| (Charpy Impact Strength(unnotched | 115 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
| Charpy Impact Strength (notched) | 4 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
| Charpy Impact Strength (notched) | 4 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
| Hardness Shore D | 77 | ISO 868 | |
| Химические свойства | |||
| Electrolytic Corrosion | IEC 60426 | ||
| Water absorption | 0.50 | % | ISO 62-at Saturation |
| Электрические свойства | |||
| Comparative Tracking Index | 575 | V | 100 drops value; IEC 60112 |
| Dissipation Factor | 0.021 | IEC 60250@Frequency 1e+6 Hz | |
| Surface Resistance | 1.00e+14 | ohm | IEC 60093 |
| Volume resistance | 1.00e+15 | ohm-cm | IEC 60093 |
| Dielectric Constant | 3.5 | IEC 60250@Frequency 1e+6 Hz | |
| Dielectric Constant | 3.3 | IEC 60250@Frequency 100 Hz | |
| Dielectric Strength | 27.0 | Kv/mm | K20/P50; IEC 60243-1 |
| Dissipation Factor | 0.0015 | IEC 60250@Frequency 100 Hz | |
| Comparative Tracking Index | 600 | V | Test Solution A CTI; IEC 60112 |