myТехнические документы
Детали
Тип продукта
зая́вки
Промышленность
Режиссер
поставщиком
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Физические свойства | |||
| Linear Mold Shrinkage | 0.017 | cm/cm | Transverse-Pigmentation can change mold shrinkage. |
| Linear Mold Shrinkage | 0.017 | cm/cm | Pigmentation can change mold shrinkage. |
| Melting range | 221 - 226 | ºC | DSC |
| MFI | 11.72 | g/10min | ISO 1133@Load 2.16 kg,Temperature 250 °C |
| Density | 1.31 | g/ml | ISO 1183 |
| Тепловые свойства | |||
| Vicat softening temperature | 220 | ºC | 10N; ISO 306 |
| Flameability | @Thickness 0.800 mm | ||
| Flameability | @Thickness 1.60 mm | ||
| Heat Deflection temperature | 150 | ºC | ISO 75-1/2-at 0.46 MPa |
| Thermal Expansion | 110 | µm/m-°C | Longitudinal; ISO 11359@Temperature 23.0-55.0 °C |
| Vicat softening temperature | 180 | ºC | 50N; ISO 306 |
| Heat Deflection temperature | 55.0 | ºC | ISO 75-1/2-at 1.8 MPa |
| Thermal Expansion | 110 | µm/m-°C | Transverse to Flow; ISO 11359@Temperature 23.0-55.0 °C |
| Glow WireTest | 850 | ºC | IEC 60695-2-1/0-3, @Thickness 2.00 mm |
| Механические свойства | |||
| Ball indentation Hardness | 150 | MPa | H30; ISO 2039-1 |
| Elongation at yield | 9.0 | % | 50 mm/min; ISO 527-1/2 |
| Hardness Shore D | 77 | ISO 868 | |
| Tensile Stress at yield-MD | 55.0 | MPa | 50 mm/min; ISO 527-1/2 |
| Tensile modulus-MD | 2600 | MPa | ISO 527-1/2 |
| (Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature 23.0 °C | |
| Elongation at break-MD | >50 | % | 50 mm/min; ISO 527-1/2 |
| (Charpy Impact Strength(unnotched | 300 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
| Charpy Impact Strength (notched) | 7 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
| Charpy Impact Strength (notched) | 6 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
| Химические свойства | |||
| Oxirane Oxygen Content | 23 | % | ISO 4589 |
| Electrolytic Corrosion | IEC 60426 | ||
| Water absorption | 0.45 | % | ISO 62 -at Saturation |
| Электрические свойства | |||
| Dielectric Strength | 27.0 | Kv/mm | K20/P50; IEC 60243-1 |
| Comparative Tracking Index | 600 | V | Test Solution A, CTI; IEC 60112 |
| Comparative Tracking Index | 575 | V | Test Solution A, 100 drops; IEC 60112 |
| Dissipation Factor | 0.023 | IEC 60250@Frequency 1e+6 Hz | |
| Dielectric Constant | 3.5 | IEC 60250@Frequency 1e+6 Hz | |
| Volume resistance | 1.00e+15 | ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 | ohm | IEC 60093 |
| Dielectric Constant | 3.3 | IEC 60250@Frequency 100 Hz | |
| Dissipation Factor | 0.0020 | IEC 60250@Frequency 100 Hz | |