Количество | Стоимость | Е диница измерения | 3амечание |
---|---|---|---|
Физические свойства | |||
Density | 1.72 | g/ml | ISO 1183 |
MFI | 22.36 | g/10min | ISO 1133@Load 2.16 kg,Temperature 250 °C |
Linear Mold Shrinkage | 0.002 | cm/cm | sheet with film gate at rim, mold temperature 80°C@Thickness 2.00 mm |
Linear Mold Shrinkage | 0.010 | cm/cm | Transverse |
Тепловые свойства | |||
Heat Deflection temperature | 206 | ºC | at 1.8 MPa-ISO 75-1/-2 |
Vicat softening temperature | 207 | ºC | Method B, 50 N; ISO 75-1/-2 |
Vicat softening temperature | 215 | ºC | Method A, 10 N; ISO 75-1/-2 |
Flameability | IEC 60695@Thickness 0.400 mm | ||
Heat Deflection temperature | 221 | ºC | at 0.46 MPa-ISO 75-1/-2 |
Flameability | IEC 60695@Thickness 1.60 mm | ||
Flameability | IEC 60695@Thickness 0.800 mm | ||
Механические свойства | |||
Creep modulus | 8500 | MPa | 1000hours-Crosslinked; ISO 899-1 |
(Charpy Impact Strength(unnotched | 60 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
Tensile Stress at break-MD | 130 | MPa | ISO 527-1/2 |
Elongation at break-MD | 1.8 | % | ISO 527-1/2 |
Tensile modulus-MD | 11000 | MPa | ISO 527-1/-2 |
(Charpy Impact Strength(unnotched | 60 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
Charpy Impact Strength (notched) | 8.5 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
Charpy Impact Strength (notched) | 8.5 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
Creep modulus | 11000 | MPa | 1hour -Uncrosslinked; ISO 899-1 |
Ball indentation Hardness | 230 | MPa | H30 (350 Kgy); ISO 2039-1 |
Creep modulus | 11000 | MPa | 1hour-Crosslinked; ISO 899-1 |
Creep modulus | 7500 | MPa | 1000hours-Uncrosslinked; ISO 899-1 |
Химические свойства | |||
Water absorption | 0.40 | % | ISO 62 -at Saturation |
Электрические свойства | |||
Dielectric Constant | 4.0 | IEC 60250@Frequency 100 Hz | |
Comparative Tracking Index | 250 | V | Test Solution A CTI; IEC 60112 |
Comparative Tracking Index | 250 | V | 100 drops value; IEC 60112 |
Surface Resistance | 1.00e+15 | ohm | IEC 60093 |
Dielectric Strength | 30.0 | Kv/mm | K20/P50; IEC 60243-1 |
Dielectric Constant | 4.0 | IEC 60250@Frequency 1e+6 Hz | |
Dissipation Factor | 0.018 | IEC 60250@Frequency 1e+6 Hz | |
Dissipation Factor | 0.0070 | IEC 60250@Frequency 100 Hz |