myТехнические документы
Description: VESTODUR X7285 is a 30% glass fiber reinforced compound based on polymer-modified polybutylene terephthalate (PBT) for injection molding. The compound is suitable for parts with high mechanical and thermal resistance.
Детали Соединение
Тип продукта
Усиленный с
Режиссер
поставщиком
Дреимущества
- high mechanical and thermal resistance
- In contrast to common glass fiber reinforced PBT compounds with comparable stiffness moldings of VESTODUR X7285 show in particular a high surface quality
Другие приложения
injection molding
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Физические свойства | |||
| MFI | 21.7 | g/10min | |
| Linear Mold Shrinkage | 0.002 | cm/cm | ;sheet with film gate at rim, mold temperature 80°C@Thickness 2.00 mm |
| Linear Mold Shrinkage | 0.015 | cm/cm | Transverse |
| Density | 1.55 | g/ml | ISO 1183 |
| MFI | 21.7 | g/10min | |
| Тепловые свойства | |||
| Flameability | IEC 60695@Thickness 0.800 mm | ||
| Vicat softening temperature | 220 | ºC | Method A, 10 N; ISO 306 |
| Vicat softening temperature | 213 | ºC | Method B, 50 N; ISO 306 |
| Flameability | IEC 60695@Thickness 1.60 mm | ||
| Heat Deflection temperature | 223 | ºC | ISO 75-1/-2; at 0.46 MPa |
| Heat Deflection temperature | 200 | ºC | ISO 75-1/-2; at 1.8 MPa |
| Механические свойства | |||
| Tensile modulus-MD | 10000 | MPa | ISO 527-1/2 |
| Elongation at break-MD | 2.7 | % | ISO 527-1/2 |
| Tensile Stress at break-MD | 150 | MPa | ISO 527-1/2 |
| Charpy Impact Strength (notched) | 11 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
| (Charpy Impact Strength(unnotched | 65 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
| (Charpy Impact Strength(unnotched | 65 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
| Charpy Impact Strength (notched) | 10 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
| Химические свойства | |||
| Water absorption | 0.50 | % | ISO 62; at Saturation |