Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Processing Temperature | 140 - 150 | ºC | Forming Temperature |
| Processing Temperature | >80.0 | ºC | Reverse Forming Temperature |
| Свойства внешнего вида | |||
| Refractive index | 1.491 | clear grade; ISO 489@Thickness 3.00 mm | |
| Физические свойства | |||
| Density | 1.19 | g/ml | ISO 1183 |
| Тепловые свойства | |||
| U Value | 5.3 | W/m² | DIN 4701; for 5 mm |
| U Value | 4.4 | W/m² | DIN 4701; for 10 mm |
| U Value | 5.8 | W/m² | DIN 4701; for 1 mm |
| Thermal Expansion | 80.0 | µm/m-°C | DIN 53752A@Temperature 0.000-50.0 °C;linear |
| Vicat softening temperature | 100 | ºC | ISO 306, Method B 50 |
| Specific Heat Capacity | 1.47 | J/gºC | |
| U Value | 5.6 | W/m² | DIN 4701; for 3 mm |
| Maximum Service Temperature | 70.0 | ºC | Permanent;air |
| Heat Deflection temperature | 98.0 | ºC | ISO 75;at 0.46 MPa |
| Heat Deflection temperature | 93.0 | ºC | ISO 75;at 1.8 MPa |
| Механические свойства | |||
| Elongation at break-MD | 15 | % | Nominal; ISO 527-2 1B/50 |
| shear modulus | 775 | MPa | Calculated |
| Tensile modulus-MD | 2200 | MPa | Short Time Value; ISO 527-2/1B/1 |
| Tensile Stress at break-MD | 50.0 | MPa | ISO 527-2/1B/5 |
| Charpy Impact Strength (notched) | 6.50 | kJ/m² | ISO 179/1eA |
| Flexural strength | 85.0 | MPa | 5 mm/min (80x10x4 mm); ISO 178 |
| (Izod impact strength(notched | 4.50 | kJ/m² | ISO 180/1A |
| Poisson's ratio | 0.42 | dilation speed of 5% per min; up to 2% dilation; ISO 527-1@Temperature 23.0 °C | |
| Abrasion | 30 - 40 | % Haze, Abrasion resistance in Taber abrader test (100 rev.;5.4 N; CS-10F); ISO 9352 | |
| Ball indentation Hardness | 130 | MPa | H961/30; ISO 2039-1 |
| (Charpy Impact Strength(unnotched | 65.0 | kJ/m² | ISO 179/1fU |
| Химические свойства | |||
| Water absorption | 0.525 | % | 24 hrs, 23°C from dry state; ISO 62, Method 1 |
| Water absorption | 2.1 | % | Max. Weight Gain During Immersion; ISO 62, Method 1; at Saturation |
| Moisture Expansion | 0.60 | % | Possible Expansion due to heat and moisture |
| Оптические свойства | |||
| Transmittance | 85 | % | Total Energy Transmittance g; clear grade, 3 mm, DIN EN 410 |
| Absorption in the Visible Range | <0.05 | % | clear grade, 3 mm |
| Transmittance | 91 | % | Visible; clear grade; DIN 5036, Part 3@Thickness 3.00 mm;visible |
| Transmittance | 0.00 | % | UV; clear grade@Thickness 3.00 mm |
| Reflection Coefficient | 0.040 | Visible (0-1); clear grade, Reflection loss in the visible range (for each surface) @Thickness 3.00 mm | |
| Электрические свойства | |||
| Volume resistance | >1.00e+14 | ohm-cm | DIN VDE 0303, Part 3 |
| Surface Resistance | >1.00e+14 | ohm | DIN VDE 0303, Part 3 |