Description: PLEXIGLAS® GS cast acrylic
Детали
Тип продукта
зая́вки
Режиссер
поставщиком
Дреимущества
- absolutely colorless
- clear break-resistant
- unequalled resistance to weathering and ageing
- high-quality surface and planarity; brilliant or satin
- good resistance to dilute acids
- limited resistance to organic solvents
- good resistance to alkalis
- very easy to work
- similar to hardwood
- easy to thermoform over wide range of conditions easily and firmly bonded, e.g. with reaction adhesives
- burns more or less like hardwood
- very little smoke generation
- max. service temperature approx. 80 °C
Другие приложения
sheets, blocks, tubes, round and square rods2 to 160 mm solid sheet / block thickness
standard size up to 3050 x 2030 mm more than 50 standard colors
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Свойства внешнего вида | |||
| Refractive index | 1.491 | clear grade; ISO 489@Thickness 3.00 mm | |
| Физические свойства | |||
| Density | 1.19 | g/ml | ISO 1183 |
| Тепловые свойства | |||
| U Value | 5.3 | W/m² | DIN 4701; for 5 mm |
| Maximum Service Temperature | 200 | ºC | IR Radiator |
| Vicat softening temperature | 115 | ºC | ISO 306, Method B 50 |
| Thermal Expansion | 70.0 | µm/m-°C | DIN 53752A@Temperature 0.000-50.0 °C;Linear |
| Heat Deflection temperature | 113 | ºC | ISO 75;at 0.46 MPa |
| Specific Heat Capacity | 1.47 | J/gºC | |
| Maximum Service Temperature | 80.0 | ºC | Permanent |
| Heat Deflection temperature | 105 | ºC | ISO 75;at 1.8 MPa |
| U Value | 5.6 | W/m² | DIN 4701; for 3 mm |
| U Value | 5.8 | W/m² | DIN 4701; for 1 mm |
| U Value | 4.4 | W/m² | DIN 4701; for 10 mm |
| Thermal Conductivity | 0.190 | W/mk | DIN 52612 |
| flash point | 425 | ºC | Ignition Temperature; DIN 51794 |
| Flameability | @Thickness 1.60 mm | ||
| Механические свойства | |||
| Poisson's ratio | 0.37 | dilation speed of 5% per min; up to 2% dilation; ISO 527-1@Temperature 23.0 °C | |
| Coefficient of friction | 0.45 | steel/plastic | |
| Coefficient of friction | 0.50 | plastic/steel | |
| Coefficient of friction | 0.80 | plastic/plastic | |
| Tensile modulus-MD | 3300 | MPa | Short Time Value; ISO 527-2/1B/1 |
| (Izod impact strength(notched | 1.60 | kJ/m² | ISO 180/1A |
| Elongation at break-MD | 5.5 | % | ISO 527-2/1B/5 |
| (Charpy Impact Strength(unnotched | 15.0 | kJ/m² | ISO 179/1fU |
| Tensile Stress at break-MD | 80.0 | MPa | ISO 527-2/1B/5 |
| Tensile strength | 40.0 | MPa | ISO 527-2/1B/5@Temperature 70.0 °C;Ultimate |
| Abrasion | 20 - 30 | ℅Haze, Abrasion resistance in Taber abrader test (100 rev.;5.4 N; CS-10F) ; ISO 9352 | |
| Flexural strength | 115 | MPa | 5mm/min (80x10x4 mm); ISO 178 |
| Ball indentation Hardness | 175 | MPa | H961/30; ISO 2039-1 |
| Tensile Stress at break-MD | 110 | MPa | ISO 527-2/1B/5@Temperature -40.0 °C |
| shear modulus | 1700 | MPa | Dynamic Shear Modulus at 10 Hz; ISO 537 |
| Compressive Strength | 110 | MPa | ISO 604; at Yield |
| Химические свойства | |||
| Water absorption | 0.48 | % | 24hrs, 23°C from dry state; ISO 62, Method 1 |
| Permeability | 8.3e-15 | g cm/cm2 h Pa | to Air |
| Permeability | 4.5e-15 | g cm/cm2 h Pa | to N2 |
| Permeability | 2.0e-14 | g cm/cm2 h Pa | to O2 |
| Moisture Vapor Transmission | 55.0 | cc-mm/m²-24hr-atm | |
| Water absorption | 2.1 | % | Max. Weight Gain During Immersion; ISO 62, Method 1; at Saturation |
| Moisture Expansion | 0.50 | % | Possible Expansion due to heat and moisture |
| Permeability | 1.1e-13 | g cm/cm2 h Pa | to CO2 |
| Оптические свойства | |||
| Transmittance | 85 | % | clear grade, 3 mm, DIN EN 410 |
| Transmittance | 92 | % | clear grade; DIN 5036, Part 3@Thickness 3.00 mm;Visible |
| Transmittance | 0.00 | % | UV ; clear grade@Thickness 3.00 mm |
| Reflection Coefficient | 0.040 | (clear grade, Reflection loss in the visible range (for each surface) @Thickness 3.00 mm;Visible(0-1 | |
| Absorption in the Visible Range | <0.05 | % | clear grade, 3 mm |
| Электрические свойства | |||
| Dissipation Factor | 0.020 | DIN VDE 0303, Part 4@Frequency 100000 Hz | |
| Dielectric Constant | 3.6 | DIN VDE 0303, Part 4@Frequency 50 Hz | |
| Dissipation Factor | 0.060 | DIN VDE 0303, Part 4@Frequency 50 Hz | |
| Comparative Tracking Index | 600 | V | DIN VDE 0303, Part 1 |
| Dielectric Strength | 30.0 | Kv/mm | DIN VDE 0303, Part 2 |
| Surface Resistance | 5.00e+13 | ohm | DIN VDE 0303, Part 3 |
| Volume resistance | >1.00e+15 | ohm-cm | DIN VDE 0303, Part 3 |
| Dielectric Constant | 2.7 | DIN VDE 0303, Part 4@Frequency 100000 Hz | |
| Shielding Effectiveness | 30 | dB | Weighted Sound Reduction Index at 6 mm |
| Shielding Effectiveness | 26 | dB | Weighted Sound Reduction Index at 4 mm |
| Shielding Effectiveness | 32 | dB | Weighted Sound Reduction Index at 10 mm |
| Dielectric Constant | 3.6 | DIN VDE 0303, Part 4@Frequency 50 Hz | |
| Dielectric Constant | 2.8 | DIN VDE 0303, Part 4@Frequency 100000 Hz | |