الوثائق الفنية
Thermoplastic, medium viscosity plastic resin for injection molding, compression molding and extrusion.
تفاصيل
نوع المنتج
تطبيقات
منتج
المورد
تطبيقات أخرى
Chemical facilities
machinery and vehicle construction
cable industry
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
الخصائص الفيزيائية | |||
MFI | 9.0 | g/10min | |
Density | 1.78 | g/ml | |
الخصائص الحرارية | |||
Heat Deflection temperature | 70 | ºC | at 1.8 MPa |
Heat Deflection temperature | 130 | ºC | at 0.46 MPa |
Thermal Expansion | 100 | µm/m-°C | Transverse to Flow@Temperature 20.0 °C |
Thermal Expansion | 100 | µm/m-°C | Parallel to Flow@Temperature 20.0 °C |
Flameability | @Thickness 1.60 mm | ||
Vicat softening temperature | 166 | ºC | 50°C/hr/50 N |
خصائص ميكانيكية | |||
Tensile Impact strength | 160 | Kj/m² | |
Charpy Impact Strength (notched) | 9 | kJ/m² | @Temperature -30.0 °C |
Charpy Impact Strength (notched) | 17 | kJ/m² | |
(Charpy Impact Strength(unnotched | 220 | kJ/m² | @Temperature -30.0 °C |
(Charpy Impact Strength(unnotched | 280 | kJ/m² | |
Elongation at yield | 8.0 | % | |
Tensile modulus-MD | 2100 | MPa | |
Elongation at break-MD | > 50 | % | |
Tensile strength | 55.0 | MPa | |
الخواص الكيميائية | |||
Water absorption | 0.00 | % | |
الخواص الكهربائية | |||
Dissipation Factor | 0.25 | @Frequency 1e+6 Hz | |
Dissipation Factor | 0.032 | @Frequency 100 Hz | |
Dielectric Strength | 21.0 | Kv/mm | |
Electrical Resistivity | 2.00e+13 | ohm-cm | |
Surface Resistance | > 1.00e+15 | ohm | |
Dielectric Constant | 8.0 | @Frequency 1e+6 Hz | |
Dielectric Constant | 10 | @Frequency 100 Hz | |
Comparative Tracking Index | 250 | V |