myالوثائق الفنية
Thermoplastic, high viscosity plastic resin for injection molding, compression molding and extrusion.
تفاصيل
نوع المنتج
تطبيقات
منتج
المورد
تطبيقات أخرى
Chemical facilities
machinery and vehicle construction
cable industry
معلومات تقنية
| كمية | قدر | وحدة | التعلیق |
|---|---|---|---|
| الخصائص الفيزيائية | |||
| Density | 1.78 | g/ml | |
| MFI | 2.0 | g/10min | |
| الخصائص الحرارية | |||
| Thermal Expansion | 100 | µm/m-°C | Parallel to Flow@Temperature 20.0 °C |
| Thermal Expansion | 100 | µm/m-°C | Transverse to Flow@Temperature 20.0 °C |
| Heat Deflection temperature | 70 | ºC | at 1.8 MPa |
| Heat Deflection temperature | 130 | ºC | at 0.46 MPa |
| Vicat softening temperature | 166 | ºC | 50°C/hr/50 N |
| Flameability | @Thickness 1.60 mm | ||
| خصائص ميكانيكية | |||
| (Charpy Impact Strength(unnotched | 260 | kJ/m² | @Temperature -30.0 °C |
| Elongation at break-MD | > 50 | % | |
| Tensile strength | 50.0 | MPa | |
| Tensile modulus-MD | 2100 | MPa | |
| Elongation at yield | 9.0 | % | |
| (Charpy Impact Strength(unnotched | kJ/m² | ||
| Charpy Impact Strength (notched) | 32 | kJ/m² | |
| Charpy Impact Strength (notched) | 11 | kJ/m² | @Temperature -30.0 °C |
| Tensile Impact strength | 210 | Kj/m² | |
| Creep modulus | 1150 | MPa | 1hour |
| Creep modulus | 900 | MPa | 1000hours |
| الخواص الكيميائية | |||
| Water absorption | 0.00 | % | |
| الخواص الكهربائية | |||
| Dielectric Constant | 8.0 | @Frequency 1e+6 Hz | |
| Dissipation Factor | 0.032 | @Frequency 100 Hz | |
| Electrical Resistivity | 8.00e+12 | ohm-cm | |
| Surface Resistance | > 1.00e+15 | ohm | |
| Dissipation Factor | 0.25 | @Frequency 1e+6 Hz | |
| Comparative Tracking Index | 250 | V | |
| Dielectric Strength | 19.0 | Kv/mm | |
| Dielectric Constant | 10 | @Frequency 100 Hz | |