Technical Documents
Thermoplastic, high viscosity plastic resin for injection molding, compression molding and extrusion.
Details
Product Type
Applications
Producer
Supplier
Other Applications
Chemical facilities
machinery and vehicle construction
cable industry
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Density | 1.78 | g/ml | |
MFI | 2.0 | g/10min | |
Thermal Properties | |||
Thermal Expansion | 100 | µm/m-°C | Parallel to Flow@Temperature 20.0 °C |
Thermal Expansion | 100 | µm/m-°C | Transverse to Flow@Temperature 20.0 °C |
Heat Deflection temperature | 70 | ºC | at 1.8 MPa |
Heat Deflection temperature | 130 | ºC | at 0.46 MPa |
Vicat softening temperature | 166 | ºC | 50°C/hr/50 N |
Flameability | @Thickness 1.60 mm | ||
Mechanical Properties | |||
(Charpy Impact Strength(unnotched | 260 | kJ/m² | @Temperature -30.0 °C |
Elongation at break-MD | > 50 | % | |
Tensile strength | 50.0 | MPa | |
Tensile modulus-MD | 2100 | MPa | |
Elongation at yield | 9.0 | % | |
(Charpy Impact Strength(unnotched | kJ/m² | ||
Charpy Impact Strength (notched) | 32 | kJ/m² | |
Charpy Impact Strength (notched) | 11 | kJ/m² | @Temperature -30.0 °C |
Tensile Impact strength | 210 | Kj/m² | |
Creep modulus | 1150 | MPa | 1hour |
Creep modulus | 900 | MPa | 1000hours |
Chemical Properties | |||
Water absorption | 0.00 | % | |
Electrical Properties | |||
Dielectric Constant | 8.0 | @Frequency 1e+6 Hz | |
Dissipation Factor | 0.032 | @Frequency 100 Hz | |
Electrical Resistivity | 8.00e+12 | ohm-cm | |
Surface Resistance | > 1.00e+15 | ohm | |
Dissipation Factor | 0.25 | @Frequency 1e+6 Hz | |
Comparative Tracking Index | 250 | V | |
Dielectric Strength | 19.0 | Kv/mm | |
Dielectric Constant | 10 | @Frequency 100 Hz |