myINFINO® GC-1250 is an eco-friendly, halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy based on 30 % post-consumer material (PCM).Can be processed using injection molding.
تفاصيل
نوع المنتج
تطبيقات
صناعة
منتج
مزايا
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
- eco-friendly
تطبيقات أخرى
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
معلومات تقنية
| كمية | قدر | وحدة | التعلیق |
|---|---|---|---|
| خصائص المظهر | |||
| Physical state | Pill | ||
| Appearance | Natural colors | ||
| الخصائص الفيزيائية | |||
| Humidity | <0.04 | % | |
| MFI | 10 | g/10min | ISO 1133;250℃/2.16kg |
| MFI | 36 | g/10min | ISO 1133;250℃/5kg |
| Shrinkage | 0.18 - 0.22 | % | (ISO 2577;Flow, 3.2 mm (MD |
| Shrinkage | 0.18 - 0.22 | % | (ISO 2577;Cross Flow, 3.2 mm (TD |
| Density | 1.39 | g/ml | ISO 1183 |
| الخصائص الحرارية | |||
| Heat Deflection temperature | 92 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Glass transition Temperature | 100 | ºC | DSC |
| Vicat softening temperature | 100 | ºC | ISO R 306;B/50 |
| UL RTI | 60 | ºC | Electric, 1.2 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical with Impact, 1.2 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical without Impact, 1.2 mm, 3.0 mm |
| Dry Time | 240 | min | |
| خصائص ميكانيكية | |||
| Strain at break-MD | 8 | % | ISO 527;5mm/min |
| Tensile modulus-MD | 4500 | MPa | ISO 527;5mm/min |
| Tensile Stress at break-MD | 40 | MPa | ISO 527;5mm/min |
| Flexural strength | 90 | MPa | ISO 178;2mm/min |
| Flexural modulus-MD | 5500 | MPa | ISO 178;2mm/min |
| (Izod impact strength(notched | 6.5 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Charpy Impact Strength (notched) | 6.5 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| Rockwell Hardness | 110 | ISO 2039-2;R Scale | |
| Tensile Stress at yield-MD | 56 | MPa | ISO 527;5mm/min |