INFINO® GC-1250 is an eco-friendly, halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy based on 30 % post-consumer material (PCM).Can be processed using injection molding.
Details
Product Type
Applications
Industry
Producer
Advantages
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
- eco-friendly
Other Applications
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Physical state | Pill | ||
Appearance | Natural colors | ||
Physical Properties | |||
Humidity | <0.04 | % | |
MFI | 10 | g/10min | ISO 1133;250℃/2.16kg |
MFI | 36 | g/10min | ISO 1133;250℃/5kg |
Shrinkage | 0.18 - 0.22 | % | (ISO 2577;Flow, 3.2 mm (MD |
Shrinkage | 0.18 - 0.22 | % | (ISO 2577;Cross Flow, 3.2 mm (TD |
Density | 1.39 | g/ml | ISO 1183 |
Thermal Properties | |||
Heat Deflection temperature | 92 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Glass transition Temperature | 100 | ºC | DSC |
Vicat softening temperature | 100 | ºC | ISO R 306;B/50 |
UL RTI | 60 | ºC | Electric, 1.2 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical with Impact, 1.2 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical without Impact, 1.2 mm, 3.0 mm |
Dry Time | 240 | min | |
Mechanical Properties | |||
Strain at break-MD | 8 | % | ISO 527;5mm/min |
Tensile modulus-MD | 4500 | MPa | ISO 527;5mm/min |
Tensile Stress at break-MD | 40 | MPa | ISO 527;5mm/min |
Flexural strength | 90 | MPa | ISO 178;2mm/min |
Flexural modulus-MD | 5500 | MPa | ISO 178;2mm/min |
(Izod impact strength(notched | 6.5 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Charpy Impact Strength (notched) | 6.5 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
Rockwell Hardness | 110 | ISO 2039-2;R Scale | |
Tensile Stress at yield-MD | 56 | MPa | ISO 527;5mm/min |