INFINO® NH-1000T is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy. Can be processed using injection molding.
تفاصيل
نوع المنتج
تطبيقات
صناعة
منتج
مزايا
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
تطبيقات أخرى
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
معلومات تقنية
| كمية | قدر | وحدة | التعلیق |
|---|---|---|---|
| خصائص المظهر | |||
| Physical state | Pill | ||
| Appearance | Natural colors | ||
| الخصائص الفيزيائية | |||
| Humidity | <0.05 | % | |
| MFI | 39 | g/10min | ISO 1133;220℃/10kg |
| Density | 1.17 | g/ml | ISO 1183 |
| الخصائص الحرارية | |||
| Heat Deflection temperature | 84 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 92 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 86 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Dry Time | 240 - 360 | min | |
| Dry Time | 120 - 240 | min | |
| UL RTI | 60 | ºC | Mechanical without Impact, 0.75 mm, 1.5 mm, 2.0 mm, 2.1 mm, 2.5 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical with Impact, 0.75 mm, 1.5 mm, 2.0 mm, 2.1 mm, 2.5 mm, 3.0 mm |
| Vicat softening temperature | 91 | ºC | ISO R 306;B/120 |
| UL RTI | 60 | ºC | Electric, 0.75 mm, 1.5 mm, 2.0 mm, 2.1 mm, 2.5 mm, 3.0 mm |
| Vicat softening temperature | 88 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 76 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| خصائص ميكانيكية | |||
| Rockwell Hardness | 114 | ISO 2039-2;R Scale | |
| Charpy Impact Strength (notched) | 39 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| (Izod impact strength(notched | 35 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Flexural modulus-MD | 2700 | MPa | ISO 178;2mm/min |
| Flexural strength | 81 | MPa | ISO 178;2mm/min |
| Tensile Stress at break-MD | 44 | MPa | ISO 527;50mm/min |
| Tensile modulus-MD | 2500 | MPa | ISO 527;50mm/min |
| Strain at break-MD | 78 | % | ISO 527;50mm/min |
| Tensile Stress at yield-MD | 54 | MPa | ISO 527;50mm/min |
| الخواص الكيميائية | |||
| Decomposition temperature | >400 | ºC | |
| الخواص الكهربائية | |||
| HAI)High Amp Arc Ignition) | 3 | arcs | 0.75mm, 1.5 mm, 2.0 mm |
| Hot Wire Ignition | 2 | s | 2.5mm, 3.0 mm |
| Volume resistance | 12e+10 | ohm-cm | |
| Hot Wire Ignition | 3 | s | 0.75mm, 1.5 mm, 2.0 mm, 2.1 mm |
| Comparative Tracking Index | V | ||
| Dielectric Strength | 22 | Kv/mm | |