Technical Documents
INFINO® NH-1000T is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy. Can be processed using injection molding.
Details
Product Type
Applications
Industry
Producer
Advantages
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
Other Applications
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Physical state | Pill | ||
Appearance | Natural colors | ||
Physical Properties | |||
Humidity | <0.05 | % | |
MFI | 39 | g/10min | ISO 1133;220℃/10kg |
Density | 1.17 | g/ml | ISO 1183 |
Thermal Properties | |||
Heat Deflection temperature | 84 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 92 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 86 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
Dry Time | 240 - 360 | min | |
Dry Time | 120 - 240 | min | |
UL RTI | 60 | ºC | Mechanical without Impact, 0.75 mm, 1.5 mm, 2.0 mm, 2.1 mm, 2.5 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical with Impact, 0.75 mm, 1.5 mm, 2.0 mm, 2.1 mm, 2.5 mm, 3.0 mm |
Vicat softening temperature | 91 | ºC | ISO R 306;B/120 |
UL RTI | 60 | ºC | Electric, 0.75 mm, 1.5 mm, 2.0 mm, 2.1 mm, 2.5 mm, 3.0 mm |
Vicat softening temperature | 88 | ºC | ISO R 306;B/50 |
Heat Deflection temperature | 76 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Mechanical Properties | |||
Rockwell Hardness | 114 | ISO 2039-2;R Scale | |
Charpy Impact Strength (notched) | 39 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
(Izod impact strength(notched | 35 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Flexural modulus-MD | 2700 | MPa | ISO 178;2mm/min |
Flexural strength | 81 | MPa | ISO 178;2mm/min |
Tensile Stress at break-MD | 44 | MPa | ISO 527;50mm/min |
Tensile modulus-MD | 2500 | MPa | ISO 527;50mm/min |
Strain at break-MD | 78 | % | ISO 527;50mm/min |
Tensile Stress at yield-MD | 54 | MPa | ISO 527;50mm/min |
Chemical Properties | |||
Decomposition temperature | >400 | ºC | |
Electrical Properties | |||
HAI)High Amp Arc Ignition) | 3 | arcs | 0.75mm, 1.5 mm, 2.0 mm |
Hot Wire Ignition | 2 | s | 2.5mm, 3.0 mm |
Volume resistance | 12e+10 | ohm-cm | |
Hot Wire Ignition | 3 | s | 0.75mm, 1.5 mm, 2.0 mm, 2.1 mm |
Comparative Tracking Index | V | ||
Dielectric Strength | 22 | Kv/mm |