Sheet Extrusion or Injection Molding, PC/ABS+CNT, Electrostatic Dissipation, Wide Processing Range, Low Surface Resistivity
تفاصيل مركب
CAS
9003-56-9
منتج
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
الخصائص الفيزيائية | |||
Specific Gravity | 1.21 | ||
MFI | 20 | g/10min | 300°C/2.16Kg |
Linear Mold Shrinkage | 0.005 - 0.007 | cm/cm | Thickness 3.2 mm |
الخصائص الحرارية | |||
Heat Deflection temperature | 110 | ºC | |
Dry Time | 300 - 420 | min | |
خصائص ميكانيكية | |||
Izod impact strength (notched) | 34.3 | J/m | Thickness 3.2 mm |
Flexural modulus-MD | 2745.86 | MPa | Thickness 6.4 mm |
Tensile strength | 58.84 | MPa | Thickness 3.2 mm |
Flexural strength | 98.06 | MPa | Thickness 6.4 mm |
Elongation at break-MD | >14 | % | Thickness 3.2 mm |
الخواص الكهربائية | |||
Surface Resistance | 1.000E+004 - 1.000E+006 | ohm | IEC 60093 |
خصائص العملية | |||
Middle Barrel Temperature | 290 - 310 | ºC | |
Mold Temperature | 60 - 80 | ºC | |
Drying Temperature | 70 - 80 | ºC |