myInjection Molding, PC/ABS Mineral Filler, General Purpose, High Stiffness, Halogen Free Flame Retardant
تفاصيل
CAS
9003-56-9
تطبيقات
منتج
معلومات تقنية
| كمية | قدر | وحدة | التعلیق |
|---|---|---|---|
| الخصائص الفيزيائية | |||
| Specific Gravity | 1.21 | ||
| Humidity | <4 | % | |
| MFI | 5 | g/10min | 250°C/2.16Kg |
| Linear Mold Shrinkage | 0.002 - 0.004 | cm/cm | Thickness 3.2 mm |
| الخصائص الحرارية | |||
| Flameability | Thickness 1-1.1 mm | ||
| UL RTI | 60 | ºC | Thickness 1-1.1 mm |
| UL RTI | 60 | ºC | Thickness 1-1.1 mm |
| UL RTI | 60 | ºC | Thickness 1-1.1 mm |
| Dry Time | 180 - 240 | min | |
| خصائص ميكانيكية | |||
| Izod impact strength (notched) | 68.6 | J/m | Thickness 3.2 mm |
| Flexural strength | 102.96 | MPa | Thickness 3.2 mm |
| Flexural modulus-MD | 4314.92 | MPa | Thickness 3.2 mm |
| Tensile strength | 58.84 | MPa | Thickness 3.2 mm |
| Elongation at break-MD | 15 | % | |
| خصائص العملية | |||
| Middle Barrel Temperature | 245 - 265 | ºC | |
| Drying Temperature | 85 - 95 | ºC | |
| Mold Temperature | 60 - 80 | ºC | |