Injection Molding, PC/ABS Mineral Filler, General Purpose, High Stiffness, Halogen Free Flame Retardant
Детали
CAS
9003-56-9
Режиссер
Технические данные
Количество | Стоимость | Е диница измерения | 3амечание |
---|---|---|---|
Физические свойства | |||
Specific Gravity | 1.21 | ||
Humidity | <4 | % | |
MFI | 5 | g/10min | 250°C/2.16Kg |
Linear Mold Shrinkage | 0.002 - 0.004 | cm/cm | Thickness 3.2 mm |
Тепловые свойства | |||
Flameability | Thickness 1-1.1 mm | ||
UL RTI | 60 | ºC | Thickness 1-1.1 mm |
UL RTI | 60 | ºC | Thickness 1-1.1 mm |
UL RTI | 60 | ºC | Thickness 1-1.1 mm |
Dry Time | 180 - 240 | min | |
Механические свойства | |||
Izod impact strength (notched) | 68.6 | J/m | Thickness 3.2 mm |
Flexural strength | 102.96 | MPa | Thickness 3.2 mm |
Flexural modulus-MD | 4314.92 | MPa | Thickness 3.2 mm |
Tensile strength | 58.84 | MPa | Thickness 3.2 mm |
Elongation at break-MD | 15 | % | |
Свойства процесса | |||
Middle Barrel Temperature | 245 - 265 | ºC | |
Drying Temperature | 85 - 95 | ºC | |
Mold Temperature | 60 - 80 | ºC |