starex® BF-0950 is an eco-friendly, scratch resistant acrylonitrile butadiene styrene (ABS) and polymethyl methacrylate (PMMA) grade. Can be processed using injection molding.
تفاصيل
تطبيقات
صناعة
منتج
مزايا
- excellent impact strength
- excellent processability & coloring properties
- good chemical resistance to especially IPA & ethanol
- excellent surface gloss
- scratch resistant
- eco-friendly
تطبيقات أخرى
Electronics / Computers > TV housings, stand base
معلومات تقنية
| كمية | قدر | وحدة | التعلیق |
|---|---|---|---|
| خصائص المظهر | |||
| Appearance | Natural colors | ||
| Physical state | Pill | ||
| الخصائص الفيزيائية | |||
| Shrinkage | 0.37 - 0.45 | % | (ISO 2577;Cross flow, 3.2 mm (TD |
| Shrinkage | 0.35 - 0.43 | % | (ISO 2577;Flow, 3.2 mm (MD |
| Humidity | <0.05 | % | |
| MFI | 13 | g/10min | ISO 1133;220℃/10kg |
| Density | 1.11 | g/ml | ISO 1183 |
| الخصائص الحرارية | |||
| Dry Time | 240 | min | |
| UL RTI | 50 | ºC | Mechanical without Impact, 1.5 mm, 3.0 mm |
| UL RTI | 50 | ºC | Mechanical with Impact, 1.5 mm, 3.0 mm |
| UL RTI | 50 | ºC | Electric, 1.5 mm, 3.0 mm |
| Vicat softening temperature | 100 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 91 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Heat Deflection temperature | 78 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| خصائص ميكانيكية | |||
| Pencil Hardness | H | JIS K 5401;500 g | |
| Rockwell Hardness | 116 | ISO 2039-2;R Scale | |
| Charpy Impact Strength (notched) | 8 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| (Izod impact strength(notched | 7 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Flexural modulus-MD | 2800 | MPa | ISO 178;2mm/min |
| Flexural strength | 85 | MPa | ISO 178;2mm/min |
| Tensile Stress at break-MD | 40 | MPa | ISO 527;50mm/min |
| Tensile modulus-MD | 2600 | MPa | ISO 527;50mm/min |
| Strain at break-MD | 20 | % | ISO 527;50mm/min |
| Tensile Stress at yield-MD | 55 | MPa | ISO 527;50mm/min |
| الخواص الكيميائية | |||
| Decomposition temperature | >400 | ºC | |