starex® BF-0950 is an eco-friendly, scratch resistant acrylonitrile butadiene styrene (ABS) and polymethyl methacrylate (PMMA) grade. Can be processed using injection molding.
Details
Applications
Industry
Producer
Advantages
- excellent impact strength
- excellent processability & coloring properties
- good chemical resistance to especially IPA & ethanol
- excellent surface gloss
- scratch resistant
- eco-friendly
Other Applications
Electronics / Computers > TV housings, stand base
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Appearance | Natural colors | ||
Physical state | Pill | ||
Physical Properties | |||
Shrinkage | 0.37 - 0.45 | % | (ISO 2577;Cross flow, 3.2 mm (TD |
Shrinkage | 0.35 - 0.43 | % | (ISO 2577;Flow, 3.2 mm (MD |
Humidity | <0.05 | % | |
MFI | 13 | g/10min | ISO 1133;220℃/10kg |
Density | 1.11 | g/ml | ISO 1183 |
Thermal Properties | |||
Dry Time | 240 | min | |
UL RTI | 50 | ºC | Mechanical without Impact, 1.5 mm, 3.0 mm |
UL RTI | 50 | ºC | Mechanical with Impact, 1.5 mm, 3.0 mm |
UL RTI | 50 | ºC | Electric, 1.5 mm, 3.0 mm |
Vicat softening temperature | 100 | ºC | ISO R 306;B/50 |
Heat Deflection temperature | 91 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
Heat Deflection temperature | 78 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Mechanical Properties | |||
Pencil Hardness | H | JIS K 5401;500 g | |
Rockwell Hardness | 116 | ISO 2039-2;R Scale | |
Charpy Impact Strength (notched) | 8 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
(Izod impact strength(notched | 7 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Flexural modulus-MD | 2800 | MPa | ISO 178;2mm/min |
Flexural strength | 85 | MPa | ISO 178;2mm/min |
Tensile Stress at break-MD | 40 | MPa | ISO 527;50mm/min |
Tensile modulus-MD | 2600 | MPa | ISO 527;50mm/min |
Strain at break-MD | 20 | % | ISO 527;50mm/min |
Tensile Stress at yield-MD | 55 | MPa | ISO 527;50mm/min |
Chemical Properties | |||
Decomposition temperature | >400 | ºC |