starex® GC-0700 H is an eco-friendly, post-consumer materials (PCM)-based acrylonitrile butadiene styrene (ABS) and polyethylene terephthalate (PET) grade. Can be processed using injection molding.
تفاصيل
تطبيقات
صناعة
منتج
مزايا
- helps in reduction of carbon emission
- good chemical resistance
- well balanced properties
- eco-friendly
تطبيقات أخرى
Automotive
Electronics / Computers > Monitors, OA machines
Telecom > Cellular phones
معاملة
It complies with the EPEAT Gold & TCO Edge eco-certifications, and RoHS regulation.
معلومات تقنية
كمية | قدر | وحدة | التعلیق |
---|---|---|---|
خصائص المظهر | |||
Appearance | Natural colors | ||
Physical state | Pill | ||
الخصائص الفيزيائية | |||
Shrinkage | 0.4 - 0.7 | % | (ASTM D955;Flow, 3.2 mm (MD |
Humidity | <0.05 | % | |
MFI | 40 | g/10min | ISO 1133;250℃/10kg |
Density | 1.09 | g/ml | ISO 1183 |
الخصائص الحرارية | |||
Dry Time | 120 - 180 | min | |
UL RTI | 60 | ºC | Mechanical without Impact, 1.5 mm, 3.0 mm |
UL RTI | 60 | ºC | Mechanical with Impact, 1.5 mm, 3.0 mm |
UL RTI | 60 | ºC | Electric, 1.5 mm, 3.0 mm |
Vicat softening temperature | 94 | ºC | ISO R 306;B/120 |
Vicat softening temperature | 90 | ºC | ISO R 306;B/50 |
Heat Deflection temperature | 97 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 89 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
Heat Deflection temperature | 85 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
Heat Deflection temperature | 73 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
Auto-ignition temperature | >400 | ºC | |
خصائص ميكانيكية | |||
Rockwell Hardness | 95 | ISO 2039-2;R Scale | |
(Izod impact strength(notched | 40 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
Flexural modulus-MD | 1761 | MPa | ISO 178;2mm/min |
Flexural strength | 49 | MPa | ISO 178;2mm/min |
Tensile Stress at break-MD | 31 | MPa | ISO 527;50mm/min |
Tensile modulus-MD | 2000 | MPa | ISO 527;50mm/min |
Strain at break-MD | 11 | % | ISO 527;50mm/min |
Tensile Stress at yield-MD | 43 | MPa | ISO 527;50mm/min |
الخواص الكيميائية | |||
Decomposition temperature | >300 | ºC |