starex® GC-0700 H is an eco-friendly, post-consumer materials (PCM)-based acrylonitrile butadiene styrene (ABS) and polyethylene terephthalate (PET) grade. Can be processed using injection molding.
Детали
Тип продукта
Промышленность
Режиссер
Дреимущества
- helps in reduction of carbon emission
- good chemical resistance
- well balanced properties
- eco-friendly
Другие приложения
Automotive
Electronics / Computers > Monitors, OA machines
Telecom > Cellular phones
Обработка
It complies with the EPEAT Gold & TCO Edge eco-certifications, and RoHS regulation.
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Свойства внешнего вида | |||
| Appearance | Natural colors | ||
| Physical state | Pill | ||
| Физические свойства | |||
| Shrinkage | 0.4 - 0.7 | % | (ASTM D955;Flow, 3.2 mm (MD |
| Humidity | <0.05 | % | |
| MFI | 40 | g/10min | ISO 1133;250℃/10kg |
| Density | 1.09 | g/ml | ISO 1183 |
| Тепловые свойства | |||
| Dry Time | 120 - 180 | min | |
| UL RTI | 60 | ºC | Mechanical without Impact, 1.5 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical with Impact, 1.5 mm, 3.0 mm |
| UL RTI | 60 | ºC | Electric, 1.5 mm, 3.0 mm |
| Vicat softening temperature | 94 | ºC | ISO R 306;B/120 |
| Vicat softening temperature | 90 | ºC | ISO R 306;B/50 |
| Heat Deflection temperature | 97 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 89 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 85 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Heat Deflection temperature | 73 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Auto-ignition temperature | >400 | ºC | |
| Механические свойства | |||
| Rockwell Hardness | 95 | ISO 2039-2;R Scale | |
| (Izod impact strength(notched | 40 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Flexural modulus-MD | 1761 | MPa | ISO 178;2mm/min |
| Flexural strength | 49 | MPa | ISO 178;2mm/min |
| Tensile Stress at break-MD | 31 | MPa | ISO 527;50mm/min |
| Tensile modulus-MD | 2000 | MPa | ISO 527;50mm/min |
| Strain at break-MD | 11 | % | ISO 527;50mm/min |
| Tensile Stress at yield-MD | 43 | MPa | ISO 527;50mm/min |
| Химические свойства | |||
| Decomposition temperature | >300 | ºC | |