| كمية | قدر | وحدة | التعلیق |
|---|---|---|---|
| الخصائص الفيزيائية | |||
| Linear Mold Shrinkage | 0.009 - 0.015 | cm/cm | sheet with film gate at rim, mold temperature 80°C @Thickness 3.00 mm; Transverse |
| Linear Mold Shrinkage | 0.0060 - 0.011 | cm/cm | sheet with film gate at rim, mold temperature 80°C @Thickness 3.00 mm |
| Density | 1.03 | g/ml | ISO 1183 |
| الخصائص الحرارية | |||
| Vicat softening temperature | 160 | ºC | 10N; ISO 306 |
| Flameability | @Thickness 1.60 mm | ||
| Vicat softening temperature | 100 | ºC | 50N; ISO 306 |
| Heat Deflection temperature | 90.0 | ºC | at 0.46 MPa;ISO 75-2 |
| Thermal Expansion | 200 | µm/m-°C | Longitudinal; ISO 11359@Temperature 23.0 -55.0 °C |
| Thermal Expansion | 200 | µm/m-°C | ISO 11359;Transverse to Flow@Temperature 23.0 -55.0 °C |
| Heat Deflection temperature | 45.0 | ºC | at 1.8 MPa;ISO 75-1 |
| خصائص ميكانيكية | |||
| (Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature 23.0 °C | |
| (Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature -30.0 °C | |
| Charpy Impact Strength (notched) | 22 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
| Hardness Shore D | 55 | ISO 868 | |
| Charpy Impact Strength (notched) | kJ/m² | ISO 179/1eA@Temperature 23.0 °C | |
| Tensile modulus-MD | 230 | MPa | ISO 527-1, ISO 527-2 |
| Elongation at break-MD | >200 | % | ISO 527-1, ISO 527-2 |
| Tensile Stress at break-MD | 38.0 | MPa | ISO 527-1, ISO 527-2 |
| Creep modulus | 100 | MPa | 1000hours;ISO 899-1 |
| viscosity number | 190 | ml/g | Viscosity Number; ISO 307 |
| الخواص الكيميائية | |||
| Water absorption | 1.1 | % | ISO 62;at Saturation |
| الخواص الكهربائية | |||
| Comparative Tracking Index | 600 | V | Test Solution A; IEC 60112 |
| Dielectric Strength | 38.0 | Kv/mm | K20/P50; IEC 60243-1 |
| Dissipation Factor | 0.095 | IEC 60250@Frequency 100 Hz | |
| Dielectric Constant | 9.5 | IEC 60250@Frequency 100 Hz | |
| Volume resistance | 1.00e+11 | ohm-cm | Spec.; IEC 60093 |
| Surface Resistance | 1.00e+13 | ohm | Spec.; IEC 60093 |
| Dielectric Constant | 4.3 | IEC 60250@Frequency 1e+6 Hz | |
| Dissipation Factor | 0.11 | IEC 60250@Frequency 1e+6 Hz | |