Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
Linear Mold Shrinkage | 0.009 - 0.015 | cm/cm | sheet with film gate at rim, mold temperature 80°C @Thickness 3.00 mm; Transverse |
Linear Mold Shrinkage | 0.0060 - 0.011 | cm/cm | sheet with film gate at rim, mold temperature 80°C @Thickness 3.00 mm |
Density | 1.03 | g/ml | ISO 1183 |
Thermal Properties | |||
Vicat softening temperature | 160 | ºC | 10N; ISO 306 |
Flameability | @Thickness 1.60 mm | ||
Vicat softening temperature | 100 | ºC | 50N; ISO 306 |
Heat Deflection temperature | 90.0 | ºC | at 0.46 MPa;ISO 75-2 |
Thermal Expansion | 200 | µm/m-°C | Longitudinal; ISO 11359@Temperature 23.0 -55.0 °C |
Thermal Expansion | 200 | µm/m-°C | ISO 11359;Transverse to Flow@Temperature 23.0 -55.0 °C |
Heat Deflection temperature | 45.0 | ºC | at 1.8 MPa;ISO 75-1 |
Mechanical Properties | |||
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature 23.0 °C | |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature -30.0 °C | |
Charpy Impact Strength (notched) | 22 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
Hardness Shore D | 55 | ISO 868 | |
Charpy Impact Strength (notched) | kJ/m² | ISO 179/1eA@Temperature 23.0 °C | |
Tensile modulus-MD | 230 | MPa | ISO 527-1, ISO 527-2 |
Elongation at break-MD | >200 | % | ISO 527-1, ISO 527-2 |
Tensile Stress at break-MD | 38.0 | MPa | ISO 527-1, ISO 527-2 |
Creep modulus | 100 | MPa | 1000hours;ISO 899-1 |
viscosity number | 190 | ml/g | Viscosity Number; ISO 307 |
Chemical Properties | |||
Water absorption | 1.1 | % | ISO 62;at Saturation |
Electrical Properties | |||
Comparative Tracking Index | 600 | V | Test Solution A; IEC 60112 |
Dielectric Strength | 38.0 | Kv/mm | K20/P50; IEC 60243-1 |
Dissipation Factor | 0.095 | IEC 60250@Frequency 100 Hz | |
Dielectric Constant | 9.5 | IEC 60250@Frequency 100 Hz | |
Volume resistance | 1.00e+11 | ohm-cm | Spec.; IEC 60093 |
Surface Resistance | 1.00e+13 | ohm | Spec.; IEC 60093 |
Dielectric Constant | 4.3 | IEC 60250@Frequency 1e+6 Hz | |
Dissipation Factor | 0.11 | IEC 60250@Frequency 1e+6 Hz |