كمية | قدر | وحدة | التعلیق |
---|---|---|---|
خصائص المظهر | |||
Appearance | White | ||
الخصائص الفيزيائية | |||
Melting range | 221 - 226 | ºC | DSC |
Linear Mold Shrinkage | 0.017 | cm/cm | Transverse-Pigmentation can change mold shrinkage. |
Linear Mold Shrinkage | 0.0030 | cm/cm | Pigmentation can change mold shrinkage. |
Density | 1.65 | g/ml | ISO 1183 |
MFI | 33 | g/10min | ISO 1133@Load 2.16 kg,Temperature 250 °C |
الخصائص الحرارية | |||
Flameability | @Thickness 0.800 mm | ||
Flameability | @Thickness 1.60 mm | ||
Vicat softening temperature | 212 | ºC | 50N; ISO 306 |
Heat Deflection temperature | 215 | ºC | ISO 75-1/2-at 1.8 MPa |
Heat Deflection temperature | 223 | ºC | ISO 75-1/2-at 0.46 MPa |
Thermal Expansion | 50.0 | µm/m-°C | Longitudinal; ISO 11359@Temperature 23.0-55.0 °C |
Vicat softening temperature | 218 | ºC | 10N; ISO 306 |
Flameability | @Thickness 0.400 mm | ||
خصائص ميكانيكية | |||
Hardness Shore D | 83 | ISO 868 | |
Charpy Impact Strength (notched) | 8 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
(Charpy Impact Strength(unnotched | 35 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
Charpy Impact Strength (notched) | 8 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
(Charpy Impact Strength(unnotched | 35 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
Tensile modulus-MD | 8000 | MPa | ISO 527-1/2 |
Elongation at break-MD | 3.0 | % | 5 mm/min; ISO 527-1/2 |
Tensile Stress at break-MD | 120.0 | MPa | 5 mm/min; ISO 527-1/2 |
الخواص الكيميائية | |||
Water absorption | 0.40 | % | ISO 62 -at Saturation |
Oxirane Oxygen Content | 34 | % | ISO 4589 |
Electrolytic Corrosion | IEC 60426 | ||
الخواص الكهربائية | |||
Dissipation Factor | 0.0030 | IEC 60250@Frequency 100 Hz | |
Dielectric Constant | 3.9 | IEC 60250@Frequency 100 Hz | |
Dielectric Strength | 27.0 | Kv/mm | K20/P50; IEC 60243-1 |
Surface Resistance | 1.00e+13 | ohm | IEC 60093 |
Dielectric Constant | 4.2 | IEC 60250@Frequency 1e+6 Hz | |
Volume resistance | 1.00e+15 | ohm-cm | IEC 60093 |
Dissipation Factor | 0.016 | IEC 60250@Frequency 1e+6 Hz | |
Comparative Tracking Index | 150 | V | Test Solution A, 100 drops; IEC 60112 |
Comparative Tracking Index | 175 | V | Test Solution A, CTI; IEC 60112 |