myТехнические документы
Детали Соединение
Тип продукта
Усиленный с
Режиссер
поставщиком
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Свойства внешнего вида | |||
| Appearance | White | ||
| Физические свойства | |||
| Melting range | 221 - 226 | ºC | DSC |
| Linear Mold Shrinkage | 0.017 | cm/cm | Transverse-Pigmentation can change mold shrinkage. |
| Linear Mold Shrinkage | 0.0030 | cm/cm | Pigmentation can change mold shrinkage. |
| Density | 1.65 | g/ml | ISO 1183 |
| MFI | 33 | g/10min | ISO 1133@Load 2.16 kg,Temperature 250 °C |
| Тепловые свойства | |||
| Flameability | @Thickness 0.800 mm | ||
| Flameability | @Thickness 1.60 mm | ||
| Vicat softening temperature | 212 | ºC | 50N; ISO 306 |
| Heat Deflection temperature | 215 | ºC | ISO 75-1/2-at 1.8 MPa |
| Heat Deflection temperature | 223 | ºC | ISO 75-1/2-at 0.46 MPa |
| Thermal Expansion | 50.0 | µm/m-°C | Longitudinal; ISO 11359@Temperature 23.0-55.0 °C |
| Vicat softening temperature | 218 | ºC | 10N; ISO 306 |
| Flameability | @Thickness 0.400 mm | ||
| Механические свойства | |||
| Hardness Shore D | 83 | ISO 868 | |
| Charpy Impact Strength (notched) | 8 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
| (Charpy Impact Strength(unnotched | 35 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
| Charpy Impact Strength (notched) | 8 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
| (Charpy Impact Strength(unnotched | 35 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
| Tensile modulus-MD | 8000 | MPa | ISO 527-1/2 |
| Elongation at break-MD | 3.0 | % | 5 mm/min; ISO 527-1/2 |
| Tensile Stress at break-MD | 120.0 | MPa | 5 mm/min; ISO 527-1/2 |
| Химические свойства | |||
| Water absorption | 0.40 | % | ISO 62 -at Saturation |
| Oxirane Oxygen Content | 34 | % | ISO 4589 |
| Electrolytic Corrosion | IEC 60426 | ||
| Электрические свойства | |||
| Dissipation Factor | 0.0030 | IEC 60250@Frequency 100 Hz | |
| Dielectric Constant | 3.9 | IEC 60250@Frequency 100 Hz | |
| Dielectric Strength | 27.0 | Kv/mm | K20/P50; IEC 60243-1 |
| Surface Resistance | 1.00e+13 | ohm | IEC 60093 |
| Dielectric Constant | 4.2 | IEC 60250@Frequency 1e+6 Hz | |
| Volume resistance | 1.00e+15 | ohm-cm | IEC 60093 |
| Dissipation Factor | 0.016 | IEC 60250@Frequency 1e+6 Hz | |
| Comparative Tracking Index | 150 | V | Test Solution A, 100 drops; IEC 60112 |
| Comparative Tracking Index | 175 | V | Test Solution A, CTI; IEC 60112 |