myالوثائق الفنية
تفاصيل مركب
نوع المنتج
معلومات تقنية
| كمية | قدر | وحدة | التعلیق |
|---|---|---|---|
| خصائص المظهر | |||
| Appearance | White | ||
| الخصائص الفيزيائية | |||
| Linear Mold Shrinkage | 0.016 - 0.018 | cm/cm | Transverse |
| MFI | 37.95 | g/10min | Temperature 250 °C, Load 2.16 k-ISO 1133@ |
| Linear Mold Shrinkage | 0.0020 - 0.0040 | cm/cm | sheet with film gate at rim, mold temperature 80°C@Thickness 2.00 mm |
| Density | 1.65 | g/ml | ISO 1183 |
| الخصائص الحرارية | |||
| Vicat softening temperature | 218 | ºC | Method A, 10 N; ISO 306 |
| Vicat softening temperature | 212 | ºC | Method B, 50 N; ISO 306 |
| Thermal Expansion | 50.0 | µm/m-°C | Longitudinal; ISO 11359, DIN 53752@Temperature 23.0 -55.0 °C |
| Flameability | IEC 60695@Thickness 0.800 mm | ||
| Flameability | IEC 60695@Thickness 1.60 mm | ||
| خصائص ميكانيكية | |||
| (Charpy Impact Strength(unnotched | 25 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
| Charpy Impact Strength (notched) | 6 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
| Charpy Impact Strength (notched) | 6 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
| Tensile modulus-MD | 8000 | MPa | ISO 527-1/-2 |
| Hardness Shore D | 83 | ISO 868 | |
| Elongation at break-MD | 2.2 | % | ISO 527-1/2 |
| (Charpy Impact Strength(unnotched | 25 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
| Tensile Stress at break-MD | 110 | MPa | ISO 527-1/2 |
| الخواص الكيميائية | |||
| Water absorption | 0.40 | % | at Saturation-ISO 62 |
| الخواص الكهربائية | |||
| Comparative Tracking Index | 175 | V | Test Solution A CTI; IEC 60112 |
| Comparative Tracking Index | 150 | V | 100 drops value; IEC 60112 |
| Volume resistance | 1.00e+16 | ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 | ohm | IEC 60093 |