Technical Documents
Details Compound
Product Type
Reinforced with
Technical data
Quantity | Value | Unit | Comment |
---|---|---|---|
Appearance Properties | |||
Appearance | White | ||
Physical Properties | |||
Linear Mold Shrinkage | 0.016 - 0.018 | cm/cm | Transverse |
MFI | 37.95 | g/10min | Temperature 250 °C, Load 2.16 k-ISO 1133@ |
Linear Mold Shrinkage | 0.0020 - 0.0040 | cm/cm | sheet with film gate at rim, mold temperature 80°C@Thickness 2.00 mm |
Density | 1.65 | g/ml | ISO 1183 |
Thermal Properties | |||
Vicat softening temperature | 218 | ºC | Method A, 10 N; ISO 306 |
Vicat softening temperature | 212 | ºC | Method B, 50 N; ISO 306 |
Thermal Expansion | 50.0 | µm/m-°C | Longitudinal; ISO 11359, DIN 53752@Temperature 23.0 -55.0 °C |
Flameability | IEC 60695@Thickness 0.800 mm | ||
Flameability | IEC 60695@Thickness 1.60 mm | ||
Mechanical Properties | |||
(Charpy Impact Strength(unnotched | 25 | kJ/m² | ISO 179/1eU@Temperature 23.0 °C |
Charpy Impact Strength (notched) | 6 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
Charpy Impact Strength (notched) | 6 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
Tensile modulus-MD | 8000 | MPa | ISO 527-1/-2 |
Hardness Shore D | 83 | ISO 868 | |
Elongation at break-MD | 2.2 | % | ISO 527-1/2 |
(Charpy Impact Strength(unnotched | 25 | kJ/m² | ISO 179/1eU@Temperature -30.0 °C |
Tensile Stress at break-MD | 110 | MPa | ISO 527-1/2 |
Chemical Properties | |||
Water absorption | 0.40 | % | at Saturation-ISO 62 |
Electrical Properties | |||
Comparative Tracking Index | 175 | V | Test Solution A CTI; IEC 60112 |
Comparative Tracking Index | 150 | V | 100 drops value; IEC 60112 |
Volume resistance | 1.00e+16 | ohm-cm | IEC 60093 |
Surface Resistance | 1.00e+13 | ohm | IEC 60093 |