MFI |
158.2 |
g/10min |
ISO 1133@Load 10.0 kg, Temperature 260 °C |
MFI |
50.85 |
g/10min |
ISO 1133@Load 5.00 kg, Temperature 250 °C |
MFI |
18.08 |
g/10min |
ISO 1133@Load 2.16 kg, Temperature 250 °C |
Density |
1.13 |
g/ml |
ISO 1183 |
Thermal Expansion |
120 |
µm/m-°C |
Longitudinal; ISO 11359, DIN 53752 @Temperature 23.0 - 80.0 °C |
Thermal Expansion |
120 |
µm/m-°C |
; ISO 11359, DIN 53752 @Temperature 23.0 - 80.0 °C ;Transverse to Flow |
Heat Deflection temperature |
130 |
ºC |
ISO 75-1/-2;at 0.46 MPa |
Heat Deflection temperature |
50.0 |
ºC |
ISO 75-1/-2;at 1.8 MPa |
Vicat softening temperature |
135 |
ºC |
Method B, 50 N; ISO 306 |
Vicat softening temperature |
80.0 |
ºC |
Method A, 10 N; ISO 306 |
Elongation at yield |
7 |
% |
ISO 527-1/2 |
Charpy Impact Strength (notched) |
10 |
kJ/m² |
ISO 179/1eA@Temperature -30.0 °C |
Charpy Impact Strength (notched) |
12 |
kJ/m² |
ISO 179/1eA@Temperature 23.0 °C |
(Charpy Impact Strength(unnotched |
|
kJ/m² |
ISO 179/1eU@Temperature -30.0 °C |
(Charpy Impact Strength(unnotched |
|
kJ/m² |
ISO 179/1eU@Temperature 23.0 °C |
Elongation at break-MD |
>50 |
% |
ISO 527-1/2 |
Tensile modulus-MD |
1500 |
MPa |
ISO 527-1/-2 |
Tensile Stress at yield-MD |
40.0 |
MPa |
ISO 527-1/2 |