Quantity | Value | Unit | Comment |
---|---|---|---|
Physical Properties | |||
MFI | 158.2 | g/10min | ISO 1133@Load 10.0 kg, Temperature 260 °C |
MFI | 50.85 | g/10min | ISO 1133@Load 5.00 kg, Temperature 250 °C |
MFI | 18.08 | g/10min | ISO 1133@Load 2.16 kg, Temperature 250 °C |
Density | 1.13 | g/ml | ISO 1183 |
Thermal Properties | |||
Thermal Expansion | 120 | µm/m-°C | Longitudinal; ISO 11359, DIN 53752 @Temperature 23.0 - 80.0 °C |
Thermal Expansion | 120 | µm/m-°C | ; ISO 11359, DIN 53752 @Temperature 23.0 - 80.0 °C ;Transverse to Flow |
Heat Deflection temperature | 130 | ºC | ISO 75-1/-2;at 0.46 MPa |
Heat Deflection temperature | 50.0 | ºC | ISO 75-1/-2;at 1.8 MPa |
Vicat softening temperature | 135 | ºC | Method B, 50 N; ISO 306 |
Vicat softening temperature | 80.0 | ºC | Method A, 10 N; ISO 306 |
Mechanical Properties | |||
Elongation at yield | 7 | % | ISO 527-1/2 |
Charpy Impact Strength (notched) | 10 | kJ/m² | ISO 179/1eA@Temperature -30.0 °C |
Charpy Impact Strength (notched) | 12 | kJ/m² | ISO 179/1eA@Temperature 23.0 °C |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature -30.0 °C | |
(Charpy Impact Strength(unnotched | kJ/m² | ISO 179/1eU@Temperature 23.0 °C | |
Elongation at break-MD | >50 | % | ISO 527-1/2 |
Tensile modulus-MD | 1500 | MPa | ISO 527-1/-2 |
Tensile Stress at yield-MD | 40.0 | MPa | ISO 527-1/2 |