myINFINO® HM-1100 is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy reinforced with glass fiber. Can be processed using injection molding.
Details Compound
Product Type
Reinforced with
Applications
Industry
Producer
Advantages
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
Other Applications
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
Technical data
| Quantity | Value | Unit | Comment |
|---|---|---|---|
| Appearance Properties | |||
| Physical state | Pill | ||
| Appearance | Natural colors | ||
| Physical Properties | |||
| MFI | 22 | g/10min | ISO 1133;220℃/10kg |
| MFI | 7 | g/10min | ISO 1133;250℃/2.16kg |
| Humidity | <0.05 | % | |
| Shrinkage | 0.1 | % | (ISO 2577;Cross Flow, 3.2 mm (TD |
| Density | 1.25 | g/ml | ISO 1183 |
| Shrinkage | 0.1 | % | (ISO 2577;Flow, 3.2 mm (MD |
| Thermal Properties | |||
| Heat Deflection temperature | 96 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Glass transition Temperature | 101 | ºC | DSC |
| Vicat softening temperature | 99 | ºC | ISO R 306;B/50 |
| UL RTI | 60 | ºC | Electric, 1.5 mm, 2.0 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical with Impact, 1.5 mm, 2.0 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical without Impact, 1.5 mm, 2.0 mm, 3.0 mm |
| Dry Time | 120 - 240 | min | |
| Heat Deflection temperature | 97 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Heat Deflection temperature | 98 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 102 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
| Mechanical Properties | |||
| Tensile Stress at yield-MD | 55 | MPa | ISO 527;5mm/min |
| Strain at break-MD | 4 | % | ISO 527;5mm/min |
| Tensile modulus-MD | 3400 | MPa | ISO 527;5mm/min |
| Tensile Stress at break-MD | 55 | MPa | ISO 527;5mm/min |
| Flexural strength | 95 | MPa | ISO 178;2mm/min |
| Flexural modulus-MD | 3800 | MPa | ISO 178;2mm/min |
| (Izod impact strength(notched | 8 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Charpy Impact Strength (notched) | 7 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| Rockwell Hardness | 118 | ISO 2039-2;R Scale | |
| Chemical Properties | |||
| Decomposition temperature | >400 | ºC | |