myINFINO® HM-1100 is a halogen free, flame retardant polycarbonate (PC) and acrylonitrile butadiene styrene (ABS) alloy reinforced with glass fiber. Can be processed using injection molding.
Детали Соединение
Тип продукта
Усиленный с
Промышленность
Режиссер
Дреимущества
- high impact strength & modulus
- high flowability
- good colorability
- excellent appearance
- well-balanced mechanical properties & processability
- halogen free
- flame retardant
Другие приложения
Electronics / Computers > TV housings, Laptops, battery, charger, note PC, OA machine and smart meter
Технические данные
| Количество | Стоимость | Е диница измерения | 3амечание |
|---|---|---|---|
| Свойства внешнего вида | |||
| Physical state | Pill | ||
| Appearance | Natural colors | ||
| Физические свойства | |||
| MFI | 22 | g/10min | ISO 1133;220℃/10kg |
| MFI | 7 | g/10min | ISO 1133;250℃/2.16kg |
| Humidity | <0.05 | % | |
| Shrinkage | 0.1 | % | (ISO 2577;Cross Flow, 3.2 mm (TD |
| Density | 1.25 | g/ml | ISO 1183 |
| Shrinkage | 0.1 | % | (ISO 2577;Flow, 3.2 mm (MD |
| Тепловые свойства | |||
| Heat Deflection temperature | 96 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Unannealed |
| Glass transition Temperature | 101 | ºC | DSC |
| Vicat softening temperature | 99 | ºC | ISO R 306;B/50 |
| UL RTI | 60 | ºC | Electric, 1.5 mm, 2.0 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical with Impact, 1.5 mm, 2.0 mm, 3.0 mm |
| UL RTI | 60 | ºC | Mechanical without Impact, 1.5 mm, 2.0 mm, 3.0 mm |
| Dry Time | 120 - 240 | min | |
| Heat Deflection temperature | 97 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Unannealed |
| Heat Deflection temperature | 98 | ºC | ISO 75-2;1.8 MPa, 4.0 mm, Annealing |
| Heat Deflection temperature | 102 | ºC | ISO 75-2;0.45 MPa, 4.0 mm, Annealing |
| Механические свойства | |||
| Tensile Stress at yield-MD | 55 | MPa | ISO 527;5mm/min |
| Strain at break-MD | 4 | % | ISO 527;5mm/min |
| Tensile modulus-MD | 3400 | MPa | ISO 527;5mm/min |
| Tensile Stress at break-MD | 55 | MPa | ISO 527;5mm/min |
| Flexural strength | 95 | MPa | ISO 178;2mm/min |
| Flexural modulus-MD | 3800 | MPa | ISO 178;2mm/min |
| (Izod impact strength(notched | 8 | kJ/m² | ISO 180 1A;at 23°C, 4 mm |
| Charpy Impact Strength (notched) | 7 | kJ/m² | ISO 179 1eA;at 23°C, 4 mm |
| Rockwell Hardness | 118 | ISO 2039-2;R Scale | |
| Химические свойства | |||
| Decomposition temperature | >400 | ºC | |